Hexcel® HexPly® F515 Epoxy Resin, T2C120 Carbon Tape

Category Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® F515 Epoxy Resin, T2C120 Carbon Tape.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hexcel designation: TXX120-12"-F515; Fiber: Toho® G30/500Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 1931 MPa

@Temperature 23.0 °C
 280100 psi

@Temperature 73.4 °F
1937 MPa

@Temperature 71.0 °C
 280900 psi

@Temperature 160 °F
 1/2 hr
Tensile Modulus 103.4 GPa

@Temperature 23.0 °C
 15000 ksi

@Temperature 73.4 °F
110.3 GPa

@Temperature 71.0 °C
 16000 ksi

@Temperature 160 °F
 1/2 hr
Flexural Yield Strength 1338 MPa

@Temperature 71.0 °C
 194100 psi

@Temperature 160 °F
 1/2 hr
1351 MPa

@Temperature 23.0 °C
 195900 psi

@Temperature 73.4 °F
Flexural Modulus 108.3 GPa

@Temperature 23.0 °C
 15710 ksi

@Temperature 73.4 °F
117.2 GPa

@Temperature 71.0 °C
 17000 ksi

@Temperature 160 °F
 1/2 hr
Compressive Yield Strength 1076 MPa

@Temperature 71.0 °C
 156100 psi

@Temperature 160 °F
 1/2 hr
1158 MPa

@Temperature 23.0 °C
 168000 psi

@Temperature 73.4 °F
Compressive Modulus 93.1 GPa

@Temperature 71.0 °C
 13500 ksi

@Temperature 160 °F
 1/2 hr
106.9 GPa

@Temperature 23.0 °C
 15500 ksi

@Temperature 73.4 °F
Shear Strength 75.8 MPa

@Temperature 71.0 °C
 11000 psi

@Temperature 160 °F
 Short Beam, 1/2 hr
92.4 MPa

@Temperature 23.0 °C
 13400 psi

@Temperature 73.4 °F