Hexcel® HexPly® 8551-7 Epoxy Matrix, IM7 Fiber

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® 8551-7 Epoxy Matrix, IM7 Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 10.9 MPa

@Temperature 25.0 °C
 1580 psi

@Temperature 77.0 °F
 Quasi tensile strength
57.9 MPa

@Temperature 25.0 °C
 8400 psi

@Temperature 77.0 °F
 Quasi tensile strength
75.8 MPa

@Temperature 25.0 °C
 11000 psi

@Temperature 77.0 °F
 90°, Dry
931 MPa

@Temperature 25.0 °C
 135000 psi

@Temperature 77.0 °F
 Quasi tensile strength
2760 MPa

@Temperature 25.0 °C
 400000 psi

@Temperature 77.0 °F
 0°, Dry
Elongation at Yield 1.0 %

@Temperature 25.0 °C
 1.0 %

@Temperature 77.0 °F
 90°, Dry
1.64 %

@Temperature 25.0 °C
 1.64 %

@Temperature 77.0 °F
 0°, Dry
Tensile Modulus 8.34 GPa

@Temperature 25.0 °C
 1210 ksi

@Temperature 77.0 °F
 90°, Dry
159 GPa

@Temperature 25.0 °C
 23100 ksi

@Temperature 77.0 °F
 0°, Dry
Compressive Yield Strength 228 MPa

@Temperature 25.0 °C
 33100 psi

@Temperature 77.0 °F
 After 3000 in-inlb/in impact
248 MPa

@Temperature 104 °C
 36000 psi

@Temperature 219 °F
 Open hole compression, Wet
255 MPa

@Temperature 82.0 °C
 37000 psi

@Temperature 180 °F
 Open hole compression, Wet
290 MPa

@Temperature 25.0 °C
 42100 psi

@Temperature 77.0 °F
 Open hole compression, Dry
303 MPa

@Temperature 25.0 °C
 43900 psi

@Temperature 77.0 °F
 After 2500 in-inlb/in impact
324 MPa

@Temperature 25.0 °C
 47000 psi

@Temperature 77.0 °F
 After 2000 in-inlb/in impact
345 MPa

@Temperature 25.0 °C
 50000 psi

@Temperature 77.0 °F
 After 1500 in-inlb/in impact
462 MPa

@Temperature 25.0 °C
 67000 psi

@Temperature 77.0 °F
 After 500 in-inlb/in impact
586 MPa

@Temperature 25.0 °C
 85000 psi

@Temperature 77.0 °F
 Unimpacted
1100 MPa

@Temperature 82.0 °C
 160000 psi

@Temperature 180 °F
 0°, Wet
1280 MPa

@Temperature 121 °C
 186000 psi

@Temperature 250 °F
 0°, Dry
1380 MPa

@Temperature 82.0 °C
 200000 psi

@Temperature 180 °F
 0°, Dry
1620 MPa

@Temperature 25.0 °C
 235000 psi

@Temperature 77.0 °F
 0°, Dry
Compressive Modulus 143 GPa

@Temperature 82.0 °C
 20700 ksi

@Temperature 180 °F
 0°, Wet
145 GPa

@Temperature 82.0 °C
 21000 ksi

@Temperature 180 °F
 0°, Dry
148 GPa

@Temperature 25.0 °C
 21500 ksi

@Temperature 77.0 °F
 0°, Dry
150 GPa

@Temperature 104 °C
 21800 ksi

@Temperature 219 °F
 0°, Wet
152 GPa

@Temperature 121 °C
 22000 ksi

@Temperature 250 °F
 0°, Dry
Shear Modulus 5.86 GPa

@Temperature 25.0 °C
 850 ksi

@Temperature 77.0 °F
 In-Plane +/- 45 tensile shear; Dry
Shear Strength 40.0 MPa

@Temperature 129 °C
 5800 psi

@Temperature 264 °F
 Short Beam, Wet
56.5 MPa

@Temperature 121 °C
 8190 psi

@Temperature 250 °F
 Short Beam, Wet
68.9 MPa

@Temperature 121 °C
 9990 psi

@Temperature 250 °F
 Short Beam, Dry
68.9 MPa

@Temperature 82.0 °C
 9990 psi

@Temperature 180 °F
 Short Beam, Wet
79.3 MPa

@Temperature 82.0 °C
 11500 psi

@Temperature 180 °F
 Short Beam, Dry
100 MPa

@Temperature 25.0 °C
 14500 psi

@Temperature 77.0 °F
 Short Beam, Dry
117 MPa

@Temperature 25.0 °C
 17000 psi

@Temperature 77.0 °F
 In-Plane +/- 45 tensile shear; Dry
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 93.3 °C
200 °F
Epoxy Matrix Limit