Fujipoly Industries SarconÂ® 85T Thin-Film TR

Category	Polymer , Thermoset , Silicone
Manufacturer	Fujipoly Industries
Trade Name	Sarcon®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Fujipoly Industries SarconÂ® 85T Thin-Film TR.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Sarcon TR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GTR is a composite of Heat Conductive Silicone Rubber and fiberglass.Information provided by Fujipoly Industries

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	74	74	60Â°C for 500 hrs; ASTM D2240
	75	75	ASTM D2240
	83	83	150Â°C for 1,000 hrs; ASTM D2240
	86	86	200Â°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield	5.058 MPa	733.6 psi
	5.411 MPa	784.8 psi	150Â°C for 1,000 hrs
	6.00 MPa	870 psi	200Â°C for 1,000 hrs
Elongation at Yield	40 %	40 %	200Â°C for 1,000 hrs
	70 %	70 %	150Â°C for 1,000 hrs
	100 %	100 %
Tear Strength	0.800 kN/m	4.56 pli

Thermal Properties	Metric	English
Maximum Service Temperature, Air	182 Â°C	360 Â°F
Minimum Service Temperature, Air	-60.0 Â°C	-76.0 Â°F
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.10e+13 ohm-cm	1.10e+13 ohm-cm	60Â°C for 500 hrs
	3.70e+14 ohm-cm	3.70e+14 ohm-cm	150Â°C for 1,000 hrs
	1.00e+15 ohm-cm	1.00e+15 ohm-cm
	6.70e+15 ohm-cm	6.70e+15 ohm-cm	200Â°C for 1,000 hrs
Dielectric Constant	4.8 @Frequency 1e+6 Hz	4.8 @Frequency 1e+6 Hz	After 1000 hrs at 150Â°C
	4.8 @Frequency 1000 Hz	4.8 @Frequency 1000 Hz	After 1000 hrs at 150Â°C
	4.9 @Frequency 1000 Hz	4.9 @Frequency 1000 Hz	After 1000 hrs at 200Â°C
	4.9 @Frequency 1e+6 Hz	4.9 @Frequency 1e+6 Hz	After 1000 hrs at 200Â°C
	4.9 @Frequency 50 Hz	4.9 @Frequency 50 Hz	After 1000 hrs at 150Â°C
	4.9 @Frequency 50 Hz	4.9 @Frequency 50 Hz	After 1000 hrs at 200Â°C
	5.0 @Frequency 1e+6 Hz	5.0 @Frequency 1e+6 Hz	After 500 hrs at 60Â°C
	5.1 @Frequency 1000 Hz	5.1 @Frequency 1000 Hz	After 500 hrs at 60Â°C
	5.2 @Frequency 50 Hz	5.2 @Frequency 50 Hz	After 500 hrs at 60Â°C
Dielectric Strength	10.0 kV/mm	254 kV/in	60Â°C for 500 hrs
	15.0 kV/mm	381 kV/in	AC 60 Hz; 150Â°C for 1,000 hrs
	15.0 kV/mm	381 kV/in	AC 60 Hz
	16.0 kV/mm	406 kV/in	AC 60 Hz; 200Â°C for 1,000 hrs
Dielectric Breakdown	10000 V	10000 V	Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor	0.0020 @Frequency 1e+6 Hz	0.0020 @Frequency 1e+6 Hz	After 1000 hrs at 150Â°C
	0.0020 @Frequency 1000 Hz	0.0020 @Frequency 1000 Hz	After 1000 hrs at 200Â°C
	0.0020 @Frequency 1e+6 Hz	0.0020 @Frequency 1e+6 Hz	After 1000 hrs at 200Â°C
	0.0020 @Frequency 1000 Hz	0.0020 @Frequency 1000 Hz
	0.0030 @Frequency 1e+6 Hz	0.0030 @Frequency 1e+6 Hz
	0.0030 @Frequency 1e+6 Hz	0.0030 @Frequency 1e+6 Hz	After 500 hrs at 60Â°C
	0.0030 @Frequency 50 Hz	0.0030 @Frequency 50 Hz
	0.0030 @Frequency 50 Hz	0.0030 @Frequency 50 Hz	After 1000 hrs at 200Â°C
	0.0030 @Frequency 50 Hz	0.0030 @Frequency 50 Hz	After 1000 hrs at 150Â°C
	0.0030 @Frequency 1000 Hz	0.0030 @Frequency 1000 Hz	After 1000 hrs at 150Â°C
	0.0090 @Frequency 1000 Hz	0.0090 @Frequency 1000 Hz	After 500 hrs at 60Â°C
	0.022 @Frequency 50 Hz	0.022 @Frequency 50 Hz	After 500 hrs at 60Â°C

Descriptive Properties	Value	Comments
Color	Gray-Green
Thermal Impedance	1.35Â°C/W	FTM P-3010; ASTM D5470