Formosa Plastics Formolene® E925 Film HDPE

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer	Formosa Plastics Corporation, USA
Trade Name	Formolene®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Formosa Plastics Formolene® E925 Film HDPE.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

High Molecular Weight High Density Polyethylene (HMW-HDPE) for Film Extrusion Formolene® E925 is a bi-modal HMW-HDPE resin designed for high dart impact strength and good processing characteristics. Formolene® E925 is well balanced in overall physical properties and provides good stiffness for thin gauge film applications. Formolene® E925 meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.Applications: Industrial Liners, T-Shirt Bags, Trash Can Liner and Heavy Duty BagsInformation provided by Formosa Plastics Corporation, USA

Physical Properties	Metric	English	Comments
Density	0.949 g/cc	0.0343 lb/in³	ASTM D1505
Thickness	12.7 microns	0.500 mil
Melt Flow	0.050 g/10 min @Load 2.16 kg, Temperature 190 °C	0.050 g/10 min @Load 4.76 lb, Temperature 374 °F	Condition E; ASTM D1238
High Load Melt Index	11 g/10 min @Load 21.6 kg, Temperature 190 °C	11 g/10 min @Load 47.6 lb, Temperature 374 °F	Condition F; ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	300 %	300 %	ASTM D882
Film Elongation at Break, TD	410 %	410 %	ASTM D882
Elmendorf Tear Strength MD	10 g	10 g	ASTM D1922
Elmendorf Tear Strength TD	25 g	25 g	ASTM D1922
Dart Drop Test	200 g	0.441 lb	ASTM D1709
Film Tensile Strength at Break, MD	62.1 MPa	9000 psi	ASTM D882
Film Tensile Strength at Break, TD	28.3 MPa	4100 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	131 °C	268 °F	DSC

Processing Properties	Metric	English	Comments
Blow-up Ratio (BUR)	4.0	4.0