Fiberfil® PP-60/TC/20/VO/ND Polypropylene Homopolymer, 20% Talc Filled, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® PP-60/TC/20/VO/ND Polypropylene Homopolymer, 20% Talc Filled, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.010 cm/cm @Thickness 3.17 mm |
0.010 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.012 cm/cm @Thickness 6.35 mm |
0.012 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 16 g/10 min | 16 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 - 95 | 90 - 95 | ASTM D785 |
| Tensile Strength, Yield | 24.8 MPa | 3600 psi | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Tensile Modulus | 3.79 GPa | 550 ksi | ASTM D638 |
| Flexural Strength | 44.1 MPa | 6400 psi | ASTM D790 |
| Flexural Modulus | 3.59 GPa | 520 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.133 J/cm @Thickness 3.17 mm |
0.250 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
Users viewing this material also viewed the following:
- Kotec Carbotex K-30MRA Polycarbonate, General Purpose, Mold Release Grade
- Momentive Performance Materials HCP Boron Nitride (BN) Powder
- Solvay TECHNYL® C 50 H2 PA6, Conditioned
- SABIC Innovative Plastics Xenoy® HX6600HP PBT+PC (Asia Pacific)
- A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene
- Hexcel® IM9 Carbon Fiber (12,000 Filaments)
- ExxonMobil Santoprene® 8281-90MED Thermoplastic Elastomer
- CMW® THERMKON® 76 Tungsten Copper parts
- BASF Nypel® 6030G HS DB BK 5830 30% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved