ExxonMobil Vistamaxx™ 3980FL Propylene-based Elastomer - High Purity, Low Gel

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO), Film Grade
Manufacturer Exxon Chemical
Trade Name Vistamaxx™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Vistamaxx™ 3980FL Propylene-based Elastomer - High Purity, Low Gel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Vistamaxx 3980FL propylene-based elastomer is an olefinic elastomer primarily composed of isostatic propylene repeat units with random ethylene distribution. It is produced using ExxonMobil Chemical's EXXPOL™ Catalyst Technology. The "FL" designates this is a high purity grade with very low gel content, making it suitable for premium and performance film and molding applications.Key Features:Suitable for a wide range of cast and blown film, molding and various polymer modification and compounding applications.Can be blended with PP, PE and other polyolefins for softening, stress-whitening and impact improvement.Excellent adhesion to conventional and metallocene PP and PE for exceptional extrusion coating, lamination and tie-layer performance.Very low seal initiation temperature combined with high seal strength when used as a sealing layer of co-extruded structures.Good optical properties.Good chemical resistance to aqueous systems and non-hydrocarbon based fluids.May be used in food contact applications (with some restrictions).EU and China RoHS compliant.Applications:Blown FilmPolymer ModificationCompoundingCast FilmMolding Uses:CompoundingFilmPackaging Availability: Africa & Middle East, Europe, North America, Asia Pacific, Latin America and South AmericaInformation provided by ExxonMobil Chemical.
Physical Properties Metric English Comments
Specific Gravity 0.878 g/cc
0.878 g/cc
ASTM D1505
Melt Flow 8.0 g/10 min
8.0 g/10 min
melt flow rate; ExxonMobil Method
3.7 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.7 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ExxonMobil Method
Mechanical Properties Metric English Comments
Hardness, Shore D 40

@Time 54000 sec
40

@Time 15.0 hour
ASTM D2240
Tensile Stress 5.60 MPa

@Strain 100 %
812 psi

@Strain 100 %
ASTM D412
5.70 MPa

@Strain 300 %
827 psi

@Strain 300 %
ASTM D412
Tensile Strength, Yield 6.80 MPa
986 psi
ASTM D412
Elongation at Yield 30 %
30 %
ASTM D412
Flexural Modulus, 1% Secant 110 MPa
16000 psi
ASTM D790
Tear Strength 81.3 kN/m
464 pli
Die C; ASTM D624
Tensile Set 85 %
85 %
ASTM D412
Thermal Properties Metric English Comments
Vicat Softening Point 76.5 °C
170 °F
ASTM D1525
Descriptive Properties Value Comments
Ethylene Content 9 wt%
ExxonMobil Method