ExxonMobil Oppalyte™ 47MW247 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Oppalyte™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Oppalyte™ 47MW247 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A super white opaque biaxially oriented polypropylene film. It is designed for use in cold seal applications where superior optics and graphics are desired.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features: Outstanding opacity and bright white backgroundExtra high yieldReduced show-throughHigh glossExceptional printability and receptivity to coatingsExcellent support for cold seal and high seal strengthFeatures: Light BarrierApplications:BakeryBiscuits/Cookie/Crackers Confectionery, ChocolateConfectionery, GumConfectionery, SugarCrisps and SnacksDry Foods and Beverage Powders Frozen Food Household and Detergents Ice Cream Uses:HFFS Flexible Packaging Processing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Inner Web Extrusion Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 0.807 g/m²/day @Temperature 23.0 °C |
0.0520 g/100 in²/day @Temperature 73.4 °F |
85% RH; ExxonMobil Method |
| 0.900 g/m²/day @Temperature 25.0 °C |
0.0580 g/100 in²/day @Temperature 77.0 °F |
75% RH; ExxonMobil Method | |
| 4.04 g/m²/day @Temperature 38.0 °C |
0.260 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method | |
| Thickness | 48.3 microns | 1.90 mil | ExxonMobil Method |
| Coating Weight | 28.5 g/m² | 17.8 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 140 % | 140 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 50 % | 50 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 1.30 GPa | 189 ksi | MD; ExxonMobil Method |
| 2.10 GPa | 305 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.60 | 0.60 | Untreated Surface; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 100 MPa | 14500 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 155 MPa | 22500 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 6.0 % @Temperature 135 °C, Time 432 sec |
6.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 6.0 % @Temperature 135 °C, Time 432 sec |
6.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 75 % | 75 % | 45°; ExxonMobil Method |
| Transmission, Visible | 16 % | 16 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Whiteness Index | 90 | |
| Yield | 24200 in2/lb |
Users viewing this material also viewed the following:
- Overview of materials for Polyetheretherketone, PEEK, Aramid Fiber Filled
- PolyChem Alloy PolyPurge N
- PolyOne Stat-Tech™ CTX 1125 PC/ABS Blend, Carbon Fiber Reinforced (discontinued **)
- Huntsman IROGRAN® CA116-203 TPU-Polyester
- GrafTech P1A1 Double-Coated Adhesive Tape
- IRPC Polimaxx Polene BM3245 PC High Density Polyethylene
- Spartech M60450 General Purpose PVC
- Techmer ES HiFill® PA6 GF50 X 50% Glass Filled
- Shin-Etsu Silicones KF-8017 Fluid
- Hippe PF CC 31 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod
Copyright © lookpolymers.com All Rights Reserved