ExxonMobil Oppalyte™ 45MW647 OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Oppalyte™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Oppalyte™ 45MW647 OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A super white opaque biaxially oriented polypropylene film acrylic coated two sides. Acrylic provides excellent aroma barrier and excellent support for printing. The film provides outstanding performance on all types of packaging machinesAvailability: Africa & Middle East, Asia Pacific and EuropeKey Features: Excellent aroma barrierOutstanding opacity, white background and reduced show-throughBroad sealing range on both sidesLow sealing threshold on both sidesHigh yieldGood stiffnessSolvent-free coatingsIdeal support for water based ink printingPrintable both sidesFeatures:Acrylic CoatedFlavor & Aroma Barrier Light BarrierApplications:BakeryBiscuits/Cookie/Crackers Box OverwrapConfectionery, ChocolateConfectionery, GumConfectionery, SugarCrisps and SnacksDry Foods and Beverage Powders Health and Beauty Care Household and Detergents Pet food Uses:Box Overwrap Flexible PackagingHFFS Flexible PackagingPre-made Bags – Flexible PackagingVFSS Flexible PackagingProcessing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic PrintingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Water Vapor Transmission 0.404 g/m²/day

@Temperature 38.0 °C
0.0260 g/100 in²/day

@Temperature 100 °F
90% RH; ExxonMobil Method
0.807 g/m²/day

@Temperature 23.0 °C
0.0520 g/100 in²/day

@Temperature 73.4 °F
85% RH; ExxonMobil Method
Oxygen Transmission Rate 698 cc/m²/day

@Temperature 23.0 °C
45.0 cc/100 in²/day

@Temperature 73.4 °F
0% RH; ExxonMobil Method
702 cc/m²/day

@Temperature 23.0 °C
45.2 cc/100 in²/day

@Temperature 73.4 °F
Wet, 75% RH; ExxonMobil Method
Thickness 45.7 microns
1.80 mil
ExxonMobil Method
Coating Weight 28.2 g/m²
17.6 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 140 %
140 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 50 %
50 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity 1.30 GPa
189 ksi
MD; ExxonMobil Method
2.10 GPa
305 ksi
TD; ExxonMobil Method
Coefficient of Friction 0.25
0.25
Both Sides; ExxonMobil Method
Seal Strength 510 g/25 mm

@Pressure 0.276 MPa,
Temperature 130 °C
510 g/in

@Pressure 40.0 psi,
Temperature 266 °F
Otto Brugger, 0.5 sec; ExxonMobil Method
Film Tensile Strength at Break, MD 100 MPa
14500 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 155 MPa
22500 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 6.0 %

@Temperature 135 °C,
Time 432 sec
6.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Shrinkage, TD 6.0 %

@Temperature 135 °C,
Time 432 sec
6.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Optical Properties Metric English Comments
Gloss 75 %
75 %
45°; ExxonMobil Method
Transmission, Visible 17 %
17 %
ExxonMobil Method
Descriptive Properties Value Comments
Heat Seal Range 90°F
36.3 psi, 0.2 sec
Whiteness Index 84
Yield 24500 in2/lb