ExxonMobil Oppalyte™ 33ICE OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Oppalyte™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Oppalyte™ 33ICE OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Coextruded white opaque, low density, biaxially oriented polypropylene film. This film is designed for the ice cream applications, and is suitable for heat seal and cold seal on HFFS lines.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:High yieldWhite opaque background and reduced show-throughHigh COF inside to optimize line efficiency for heat seal applicationsWell adapted to cold seal processTreated layer must be varnished to ensure good runnability on HFFS machineFeatures: In Lamination Lap SealableLight BarrierApplications: Frozen Food Ice Cream Uses: HFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 33.0 microns | 1.30 mil | ExxonMobil Method |
| Coating Weight | 20.2 g/m² | 12.6 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 140 % | 140 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 50 % | 50 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 1.30 GPa | 189 ksi | MD; ExxonMobil Method |
| 2.10 GPa | 305 ksi | TD; ExxonMobil Method | |
| Seal Strength | 300 g/25 mm @Pressure 0.276 MPa, Temperature 130 °C |
300 g/in @Pressure 40.0 psi, Temperature 266 °F |
Otto Brugger, 0.2 sec; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 100 MPa | 14500 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 155 MPa | 22500 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 6.0 % @Temperature 135 °C, Time 432 sec |
6.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 6.0 % @Temperature 135 °C, Time 432 sec |
6.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 75 % | 75 % | 45°; ExxonMobil Method |
| Transmission, Visible | 24 % | 24 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Seal Range | 54°F | 36.3 psi, 0.2 sec |
| Yield | 34300 in2/lb |
Users viewing this material also viewed the following:
- PolyOne Nymax™ ND 1233 GF Black Polyamide 66 (Nylon 66)
- ExxonMobil Escorene® LL-3105 LLDPE/Hexene Premium Film Resin, Tough (discontinued **)
- Ravago Manufacturing Americas Hylon® N1025HLFR Nylon 6/6 (DAM) (discontinued **)
- Menzolit Menzolit® BMC 0180 Unsaturated Polyester UP
- Solvay Specialty Polymers Hylar® 5000 Polyvinylidene Fluoride (PVDF)
- ChevronTexaco Cepheus® 150
- Chosun Refractories CTL ASP-N Monolithic Refractories for Ladle and Tundish
- Dow Everest™ 200 Latex Modified Acrylic Emulsion
- 3M 3179 (Clear) Polyethylene Protective Tapes
- ExxonMobil Mobil Jet Oil II
Copyright © lookpolymers.com All Rights Reserved