ExxonMobil Metallyte™ 38MW280 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Metallyte™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Metallyte™ 38MW280 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A super white opaque biaxially oriented polypropylene film, metalized on one side. Ideal for single web packaging applications on HFFS in combination with cold seal.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features: Outstanding opacity and light barrierGood moisture barrierExcellent adhesion of aluminum to filmExtra high yieldExcellent metal appearanceBright white background one sideHigh glossExceptional printability and receptivity to coatingsExcellent support for cold seal with high seal strengthFeatures:Light BarrierApplications:BakeryBiscuits/Cookie/Crackers Confectionery, Chocolate Confectionery, Gum Confectionery, Sugar Frozen FoodHealth and Beauty CareHousehold and DetergentsPet Food Uses: Box Overwrap Flexible PackagingHFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 2.02 g/m²/day @Temperature 38.0 °C |
0.130 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method |
| Thickness | 38.1 microns | 1.50 mil | ExxonMobil Method |
| Coating Weight | 23.2 g/m² | 14.5 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 140 % | 140 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 50 % | 50 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 2.10 GPa | 305 ksi | TD; ExxonMobil Method |
| 7.508 GPa | 1089 ksi | MD; ExxonMobil Method | |
| Film Tensile Strength at Break, MD | 100 MPa | 14500 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 155 MPa | 22500 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 6.0 % @Temperature 135 °C, Time 432 sec |
6.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 6.0 % @Temperature 135 °C, Time 432 sec |
6.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Optical Density | 2.3 | 2.3 | ExxonMobil Method |
| Gloss | 75 % | 75 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Whiteness Index | 90 | |
| Yield | 29800 in2/lb |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable W1200 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Network Polymers PC-1015R
- Total Finathene® 2344 HDPE film (discontinued **)
- Global PP-3370-RM Polypropylene Random Copolymer
- Teknor Apex MF-87-L081A Polyvinyl Chloride, Flexible Film
- Total PPM R020 Polypropylene, Random Copolymer for Medical Grade
- Dow Corning SYL-OFF® PMCP7069 Release Modifier
- ExxonMobil Exxtral™ LNT 010 Performance Polyolefin
- Eurostar Starflam RF0055E PA66/6, 25% Glass Filled, Injection Molded
- Solvay Specialty Polymers Algoflon® A.15 PTFE (Polytetrafluoroethylene) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved