Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade |
Manufacturer | Exxon Chemical |
Trade Name | |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | ExxonMobil LLP8360.29 Rotational Molding Resin.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM D4883 |
ESCR 100% Igepal® | >= 1000 hour | >= 1000 hour | ASTM D1693 |
ESCR 10% Igepal® | 650 hour | 650 hour | ASTM D1693 |
Melt Flow | 5.20 g/10 min @Load 2.16 kg, Temperature 190 °C |
5.20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 15.2 MPa | 2200 psi | 2.0 in/min; ASTM D638 |
Elongation at Yield | 20 % | 20 % | 2.0 in/min; ASTM D638 |
Flexural Modulus | 0.600 GPa | 87.0 ksi | 1% secant; ASTM D790 |
Impact Test | 88.1 J @Thickness 3.17 mm, Temperature -40.0 °C |
65.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F |
ARM |
217 J @Thickness 6.35 mm, Temperature -40.0 °C |
160 ft-lb @Thickness 0.250 in, Temperature -40.0 °F |
ARM |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Melting Point | 125 °C | 257 °F | ASTM D3418 |
Deflection Temperature at 0.46 MPa (66 psi) | 55.0 °C | 131 °F | ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 37.0 °C | 98.6 °F | ASTM D648 |