ExxonMobil LL 1237x98 Cast Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LL 1237x98 Cast Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LL 1237x70 is a butene LLDPE with improved stiffness. It can be used alone or as a component in packaging and industrial film.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ExxonMobil Method |
| Melt Flow | 3.65 g/10 min | 3.65 g/10 min | ASTM D1238 |
| Antiblock Level | 7500 ppm | 7500 ppm | |
| Slip Level | 1500 ppm | 1500 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 8.34 MPa | 1210 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.07 MPa | 1170 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 530 % | 530 % | ASTM D882 |
| Film Elongation at Break, TD | 700 % | 700 % | ASTM D882 |
| Puncture Energy | 0.452 J | 0.333 ft-lb | ExxonMobil |
| Elmendorf Tear Strength, MD | 1.48 g/micron | 37.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 10.33 g/micron | 262.5 g/mil | ASTM D1922 |
| Dart Drop | <= 2.46 g/micron | <= 62.5 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 39.2 MPa | 5690 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 19.0 MPa | 2760 psi | ASTM D882 |
| 1% Secant Modulus, MD | 154 MPa | 22400 psi | ASTM D882 |
| 1% Secant Modulus, TD | 153.4 MPa | 22250 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 124 °C | 255 °F | Peak Melting Temperature; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 5.4 % | 5.4 % | ASTM D1003 |
| Gloss | 81 % | 81 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WEJB400L Polyvinyl Chloride, Flexible (PVC, Flexible)
- MV Labs YB800 Yb2O3 Ytterbium oxide
- Shandong Dongyue Shenzhou New Material Co CHFM 025 Perfluorosulfonic Acid Proton Exchange Membrane (PFSAPEM)
- SABIC Innovative Plastics LNP STAT-KON Noryl_HMC1508 PPE+HIPS (Europe-Africa-Middle East)
- Teknor Apex MONPRENE® MP 2770 Thermoplastic Elastomer
- Plenco 1530 Polyester, Briquette, Injection Molded
- Tisan TISARBON® UNR Polycarbonate
- ChevronTexaco ISO 460 Synthetic Wheel Motor Lubricant EP
- Braskem Prisma 2400 RACO Random Polypropylene Copolymer
- 3M Scotchlite™ 680-85 Reflective Graphic Film
Copyright © lookpolymers.com All Rights Reserved