ExxonMobil LDPE LD 306.75 Low Density Polyethylene Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Exxon Chemical
Trade Name	LDPE
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LDPE LD 306.75 Low Density Polyethylene Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 306 resins are 5.5% vinyl acetate copolymer, high clarity film resins. Film made from these resins exhibit superior impact strength and heat sealability.Availability: Latin America, North America and South America Additive: Antiblock: 3000 ppmSlip: 1100 ppm Thermal Stabilizer: YesApplications: Coextrusion FilmsFoamsForm Fill and Seal PackagingFreezer FilmHigh Clarity FilmLamination FilmPoultry BagProduce BagsRice BagsInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.925 g/cc	0.0334 lb/in³	ExxonMobil method
Vinyl Acetate Content	5.5 %	5.5 %	ExxonMobil Method
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Antiblock Level	3000 ppm	3000 ppm
Slip Level	1100 ppm	1100 ppm

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	190 %	190 %	ASTM D882
Film Elongation at Break, TD	590 %	590 %	ASTM D882
Puncture Energy	1.36 J	1.00 ft-lb	ExxonMobil Method
Elmendorf Tear Strength MD	160 g	160 g	ASTM D1922
Elmendorf Tear Strength TD	80 g	80 g	ASTM D1922
Dart Drop Test	170 g	0.375 lb	ASTM D1709A
Film Tensile Strength at Break, MD	248 MPa	36000 psi	ASTM D882
Film Tensile Strength at Break, TD	24.1 MPa	3500 psi	ASTM D882
1% Secant Modulus, MD	124 MPa	18000 psi	ASTM D882
1% Secant Modulus, TD	145 MPa	21000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 216 °C	<= 421 °F	Peak Melting Point; ExxonMobil method

Optical Properties	Metric	English	Comments
Haze	4.0 %	4.0 %	ASTM D1003
Gloss	74 %	74 %	45°; ASTM D2457

Descriptive Properties	Value	Comments
Puncture Force	11 lbf	ExxonMobil Method