ExxonMobil LDPE LD 143.26 Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Exxon Chemical
Trade Name LDPE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LDPE LD 143.26 Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 143.26 is a homopolymer packaging film resin with excellent clarity and good stiffness. It is suitable for processing in either blown or cast film equipment. In blown film equipment LD 143.26 resin can be drawn down to 1.0 mil.Availability: Latin America, North America and South America Additive: Antiblock: 1500 ppmSlip: 750 ppmThermal Stabilizer: YesApplications: Blend PartnerCast FilmDisplay Packaging FilmFood PackagingForm Fill and Seal PackagingHigh Clarity FilmLamination FilmLight Duty Shrink FilmMail BagProduce BagsTextile Packaging Information provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.923 g/cc
0.0333 lb/in³
ExxonMobil method
Melt Flow 2.1 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.1 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 1500 ppm
1500 ppm
Slip Level 750 ppm
750 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.0 MPa
1600 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D882
Film Elongation at Break, MD 190 %
190 %
ASTM D882
Film Elongation at Break, TD 550 %
550 %
ASTM D882
Puncture Energy 0.463 J
0.342 ft-lb
ExxonMobil Method
Elmendorf Tear Strength MD 380 g
380 g
ASTM D1922
Elmendorf Tear Strength TD 160 g
160 g
ASTM D1922
Dart Drop Test 80.0 g
0.176 lb
ASTM D1709A
Film Tensile Strength at Break, MD 24.1 MPa
3500 psi
ASTM D882
Film Tensile Strength at Break, TD 20.0 MPa
2900 psi
ASTM D882
1% Secant Modulus, MD 207 MPa
30000 psi
ASTM D882
1% Secant Modulus, TD 248 MPa
36000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 232 °C
<= 450 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 6.2 %
6.2 %
ASTM D1003
Gloss 72 %
72 %
45°; ASTM D2457
Descriptive Properties Value Comments
Puncture Force 7 lbf
ExxonMobil Method