ExxonMobil LD 051.LJ Molding, Extrusion and Compounding Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LD 051.LJ Molding, Extrusion and Compounding Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LD 051.LJ resin is used in Blow molded, squeeze bottles, Pail lids, Closures, and Extruded profiles.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ExxonMobil Method |
| Melt Flow | 0.25 g/10 min | 0.25 g/10 min | ASTM D1238 |
| Antiblock Level | 4000 ppm | 4000 ppm | |
| Slip Level | 500 ppm | 500 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 80 | 80 | 15 s; ASTM D2240 |
| Hardness, Shore D | 42 | 42 | 15s; ASTM D2240 |
| Tensile Strength at Break | 14.5 MPa | 2100 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Elongation at Break | 725 % | 725 % | ASTM D638 |
| Elongation at Yield | 45 % | 45 % | ASTM D638 |
| Flexural Modulus | 0.214 GPa | 31.0 ksi | 1% secant; ASTM D790 |
| Impact Test | 23.0 J | 17.0 ft-lb | Instrumented Impact Total Energy; ASTM D3763 |
| 31.2 J @Temperature -40.0 °C |
23.0 ft-lb @Temperature -40.0 °F |
Instrumented Impact, Total Energy; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 109 °C | 229 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 92.2 °C | 198 °F | ASTM D1525 |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PE 4550N (50401M) High Density Polyethylene
- SYNTHOS Koplen® 1640 F Expandable Polystyrene
- Techmer ES HiFill® PA6/6 GF33 LE 33% Glass Filled
- Saint-Gobain COHRlastic® R10470 Firm General-Purpose Silicone Sponge Rubber
- Toyobo Vylopet® EMC415 PET/PBT Blend
- Eastman Eastar MN004 Copolyester
- Asahi Kasei Thermylene® P6-30FG-0877A 30% Glass Fiber Reinforced, UV Stabilized
- Arlon 30580R020 0.020" (0.508 mm) Uncured Unsupported Silicone Rubber on Kodacel Carrier
- BASF Neopolen® P 8015 0.03 g/cc Core density; Expanded Polypropylene (Europe)
- H.C. Starck Amperit® 415.072 CoNiCrAlY (MCrAlY)
Copyright © lookpolymers.com All Rights Reserved