ExxonMobil HD 9856B Blow Molding Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer	Exxon Chemical
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil HD 9856B Blow Molding Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: HD 9856B is a HDPE blow molding resin designed for high performance packaging applications. Containers made from HD 9856B exhibit a unique combination of stiffness and environmental stress cracking resistance. These properties, coupled with excellent processability on both continuous and intermittent equipment, afford significant lightweighting and/or fast-cycling potential in many applications. HD 9856B does not contain any antistatic.Availability: Latin America, North America and South America Additive: Thermal Stabilizer: YesAntistatic: NoUV Stabilizer: NoApplications: Caps and ClosuresCompression MoldingsFood packagingHousehold and Industrial chemical containersPharmaceutical PackagingThermoformed PartsThin Gauge SheetInformation provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.957 g/cc	0.0346 lb/in³	ASTM D4883
Environmental Stress Crack Resistance	>= 1000 hour	>= 1000 hour	100% Igepal; ASTM D1693
Melt Flow	0.46 g/10 min @Load 2.16 kg, Temperature 190 °C	0.46 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	24.1 MPa	3500 psi	ASTM D638
Tensile Strength, Yield	30.3 MPa	4400 psi	ASTM D638
Elongation at Break	1100 %	1100 %	ASTM D638
Flexural Modulus	1.45 GPa	210 ksi	1% Secant; ASTM D790
Tensile Impact Strength	252 kJ/m²	120 ft-lb/in²	ASTM D1822

Thermal Properties	Metric	English	Comments
Brittleness Temperature	<= -76.1 °C	<= -105 °F	ASTM D746

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer