ExxonMobil Escorene® HDZ-123 HMW-HDPE Blown Film Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene® HDZ-123 HMW-HDPE Blown Film Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, Exxon Chemical.A high molecular weight HDPE blown film resin. Films made from HDZ-123 exhibit excellent impact and toughness properties as well as high stiffness. HDZ-123 is particularly recommended for films 0.5 mil or greater in thickness.Applications: Retail carry-out sacks; Merchandise bags; Institutional can liners; Consumer trash bags. Data for film properties below based on 0.5 mil film.

Physical Properties	Metric	English	Comments
Density	0.952 g/cc	0.0344 lb/in³	Exxon Method
Thickness	12.7 microns	0.500 mil
Melt Flow	0.045 g/10 min	0.045 g/10 min	Exxon Method (I2). HLMI (I21) is 8 g/10 min.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	39.0 MPa	5660 psi	ASTM D882
Film Tensile Strength at Yield, TD	33.0 MPa	4790 psi	ASTM D882
Film Elongation at Break, MD	300 %	300 %	ASTM D882
Film Elongation at Break, TD	400 %	400 %	ASTM D882
Secant Modulus, MD	0.965 GPa	140 ksi	ASTM D882
Secant Modulus, TD	1.14 GPa	165 ksi	ASTM D882
Elmendorf Tear Strength, MD	0.591 g/micron	15.0 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	3.15 g/micron	80.0 g/mil	ASTM D1922
Dart Drop	24.6 g/micron	625 g/mil	F50; ASTM D-1709
Film Tensile Strength at Break, MD	93.0 MPa	13500 psi	ASTM D882
Film Tensile Strength at Break, TD	72.0 MPa	10400 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	129 °C	264 °F	Exxon Method