ExxonMobil Escorene™ FL 00209 Ethylene Vinyl Acetate Copolymer (European Grade)

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer	Exxon Chemical
Trade Name	Escorene™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene™ FL 00209 Ethylene Vinyl Acetate Copolymer (European Grade).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: FL 00209 is a copolymer of ethylene and vinyl acetate. Processing Conditions: Processing temperatures above 270°C (518°F) may cause resin degradation. Machines should always be purged with LDPE or suitable cleaning compound before shutdown.Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: NoThermal Stabilizer: No Applications: Closures and DispensersCompoundingFood packagingInjection Molding Lamination FilmInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.931 g/cc	0.0336 lb/in³	ExxonMobil method
Vinyl Acetate Content	9.4 %	9.4 %	ExxonMobil method
Melt Flow	2.1 g/10 min @Load 2.16 kg, Temperature 190 °C	2.1 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	93 @Time 15.0 sec	93 @Time 0.00417 hour	Molded Properties; ISO 868
Film Elongation at Break, MD	550 %	550 %	ASTM D882
Film Elongation at Break, TD	650 %	650 %	ASTM D882
Tensile Modulus	0.0896 GPa	13.0 ksi	Molded Properties; ISO 527-2
Elmendorf Tear Strength MD	120 g	120 g	ASTM D1922
Elmendorf Tear Strength TD	190 g	190 g	ASTM D1922
Dart Drop Test	390 g	0.860 lb	ASTM D1709A
Film Tensile Strength at Break, MD	28.3 MPa	4100 psi	ASTM D882
Film Tensile Strength at Break, TD	26.9 MPa	3900 psi	ASTM D882
1% Secant Modulus, MD	89.6 MPa	13000 psi	ASTM D882
1% Secant Modulus, TD	96.5 MPa	14000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 207 °C	<= 405 °F	Peak Melting Point; ExxonMobil method
Vicat Softening Point	78.3 °C	173 °F	ASTM D1525

Descriptive Properties	Value	Comments
Blending Temperature	270