ExxonMobil ESCOR™ AT 320 Blown Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Acrylic Acid , Ethylene Methyl Acrylate
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil ESCOR™ AT 320 Blown Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ESCOR AT 320 provides excellent adhesion to a variety of substrates and other film components such as aluminum foil, polyolefins, polycarbonate, PET, etc.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Methyl Acrylate Content 18 %
18 %
Acrylic Acid Content 6.0 %
6.0 %
Melt Flow 5.0 g/10 min
5.0 g/10 min
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 330 %
330 %
ASTM D882
Film Elongation at Break, TD 600 %
600 %
ASTM D882
Elmendorf Tear Strength, MD 1.38 g/micron
35.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 11.8 g/micron
300 g/mil
ASTM D1922
Dart Drop 7.48 g/micron
190 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 20.7 MPa
3000 psi
ASTM D882
Film Tensile Strength at Break, TD 23.9 MPa
3470 psi
ASTM D882
1% Secant Modulus, MD 27.8 MPa
4030 psi
ASTM D882
1% Secant Modulus, TD 27.1 MPa
3930 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 72.2 °C
162 °F
Peak Melting Temperature; ExxonMobil Method
Descriptive Properties Value Comments
Features Thermal Stabilizer