ExxonMobil Bicor® 420 HS OPP Film
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor® 420 HS OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor HS is a two-side coated, sealable OPP film designed for general use in overwrap and horizontal packaging. This film is suitable as an unsupported web or lamination. It can be surface printed, or used unprinted.Availability: Latin America, North America and South AmericaKey Features:Outstanding optical propertiesRobust machinablityLow and consistent COFExcellent hot slipExcellent flavor and aroma barrierPrintable on both sidesFeatures:Acrylic CoatedFlavor & Aroma BarrierIn Lamination Lap SealableApplications:Biscuits/Cookie/CrackersBox OverwrapConfectionery, GumConfectionery, SugarUses:Box Overwrap Flexible PackagingHFF Flexible PackagingPre-made Bags - Flexible PackagingTobacco Overwrap Flexible PackagingProcessing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic Printing Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 7.60 g/m²/day | 0.489 g/100 in²/day | 38°C, 90% RH; ExxonMobil Method |
| Thickness | 17.8 microns | 0.700 mil | Nominal; ExxonMobil Method |
| Coating Weight | 16.5 g/m² | 10.3 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Coefficient of Friction | 0.22 | 0.22 | ExxonMobil Method |
| Film Tensile Strength at Break, MD | 138 MPa | 20000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.5 % | 4.5 % | at 275°F; ExxonMobil Method |
| Shrinkage, TD | 4.5 % | 4.5 % | at 275°F; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.5 % | 1.5 % | ExxonMobil Method |
| Gloss | 90 % | 90 % | 45º; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Crimp Seal MST | 182°F | |
| Crimp Seal Strength | 540 g/in | 260°F, 20psi, 3/4sec |
| Yield | 42000 in2/lb |
Users viewing this material also viewed the following:
- Murtfeldt Original Material ”S”® plus + ESD Polyethylene, Conductive
- Nilit FRIANYL A63 H Nylon 6.6 for injection molding
- SABIC Innovative Plastics ULTEM 2300F PEI (Europe-Africa-Middle East)
- Hexcel® HexForce™ 1526 Fiber Glass Fabric
- Hexcel® HexPly® ES70 120°C Curing Epoxy Matrix, E-glass Balanced fabric 300 g/m2
- Dow Corning SILASTIC® Q7-4735 BIOMEDICAL GRADE ETR ELASTOMER, KIT
- Covestro Desmopan® DP 9392AU Polyurethane
- BASF Capron® 8333G HI HS BK-102 Impact Modified, 33% Glass-Filled Nylon 6 (Dry) (discontinued **)
- PSM Industries Pacific Sintered Metals High Carbon Copper Steel FCC-214-S(HT) Powdered Metal
Copyright © lookpolymers.com All Rights Reserved