ExxonMobil Bicor™ 32MB777 OPP Film

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Exxon Chemical
Trade Name	Bicor™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Bicor™ 32MB777 OPP Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: A high gas barrier, biaxially oriented transparent polypropylene film, coated one side PVdC, one side acrylic. This film provides outstanding performance on all packaging machines.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Excellent moisture, oxygen and aroma barriers Excellent seal strength and hot tackExcellent retention of PVdC seals in humid conditionsOutstanding optical propertiesIdeal support for water based ink printing on acrylic sideWater based coatingsFeatures:Acrylic CoatedFlavor & Aroma BarrierGas BarrierHumidity ResistantIn Lamination Lap SealableMoisture BarrierOxygen BarrierVery PVdC CoatedApplications:BakeryBiscuits/Cookie/CrackersBox OverwrapConfectionery, Chocolate Confectionery, Gum Confectionery, SugarCrisps and SnacksDairy ProductsDry Foods and Beverage Powders Health and Beauty CareHousehold and DetergentsIce CreamPet Food Uses: Box Overwrap Flexible PackagingHFFS Flexible PackagingPre-made – Flexible PackagingVFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Water Vapor Transmission	0.807 g/m²/day @Temperature 23.0 °C	0.0520 g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	3.88 g/m²/day @Temperature 38.0 °C	0.250 g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Oxygen Transmission Rate	20.0 cc/m²/day @Temperature 23.0 °C	1.29 cc/100 in²/day @Temperature 73.4 °F	Wet, 75% RH; ExxonMobil Method
	20.2 cc/m²/day @Temperature 23.0 °C	1.30 cc/100 in²/day @Temperature 73.4 °F	0% RH; ExxonMobil Method
Thickness	33.0 microns	1.30 mil	ExxonMobil Method
Coating Weight	29.9 g/m²	18.7 lb/ream	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	175 %	175 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD	60 %	60 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity	2.00 GPa	290 ksi	MD; ExxonMobil Method
	3.80 GPa	551 ksi	TD; ExxonMobil Method
Coefficient of Friction	0.25	0.25	Acrylic; ExxonMobil Method
	0.35	0.35	PVdC; ExxonMobil Method
Seal Strength	510 g/25 mm @Pressure 0.276 MPa, Temperature 140 °C	510 g/in @Pressure 40.0 psi, Temperature 284 °F	PVdC, 0.2 sec; ExxonMobil Method
	610 g/25 mm @Pressure 0.276 MPa, Temperature 130 °C	610 g/in @Pressure 40.0 psi, Temperature 266 °F	Acrylic, 0.2 sec; ExxonMobil Method
Film Tensile Strength at Break, MD	160 MPa	23200 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

Thermal Properties	Metric	English	Comments
Shrinkage, MD	6.0 % @Temperature 135 °C, Time 432 sec	6.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method
Shrinkage, TD	5.5 % @Temperature 135 °C, Time 432 sec	5.5 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	1.7 %	1.7 %	ExxonMobil Method
Gloss	98 %	98 %	45°; ExxonMobil Method

Descriptive Properties	Value	Comments
Carbon Dioxide Transmission Rate	5.16 cc/100 in²/ 24 hr	75% RH, ASTM D1434
Heat Seal Range	54°F	PVdC, 36.3 psi, 0.2 sec
	90°F	Acrylic, 36.3 psi, 0.2 sec
Nitrogen Transmission Rate	0.645 cc/100 in²/ 24 hr	75% RH, ASTM D1434
Yield	23100 in²/lb