ExxonMobil Bicor® 125 BSR-ONE OPP Film
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor® 125 BSR-ONE OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor BSR-ONE is a two-side sealable, one side treated, coextruded OPP film designed for unsupported plain or surface print applications, and in laminations on both HFFS and VFFS packaging machines.Availability: Latin America, North America and South AmericaKey Features:Excellent machinablityStable COFExcellent hot tackExcellent hot slipExcellent hot jaw releaseExcellent heat seal strengthWide heat seal range on the untreated side (80°F/45°C)Non-migratory slip system for consistent COFFeatures:In Lamination Lap SealableApplications:BakeryBiscuts/Cookie/CrackersBox OverwrapConfectionery, GumConfectionery, SugarCrips and SnacksFrozen FoodPet FoodUses:Box Overwrap Flexible PackagingHFFS Flexible PackagingPre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 4.20 g/m²/day | 0.270 g/100 in²/day | 38°C, 90% RH; ExxonMobil Method |
| Thickness | 33.0 microns | 1.30 mil | Nominal; ExxonMobil Method |
| Coating Weight | 28.2 g/m² | 17.6 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Coefficient of Friction | 0.34 | 0.34 | Treated; ExxonMobil Method |
| 0.39 | 0.39 | Untreated; ExxonMobil Method | |
| Film Tensile Strength at Break, MD | 124 MPa | 18000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 255 MPa | 37000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 % | 5.0 % | at 275°F; ExxonMobil Method |
| Shrinkage, TD | 4.5 % | 4.5 % | at 275°F; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.3 % | 2.3 % | ExxonMobil Method |
| Gloss | 85 % | 85 % | 45°, Treated Surface; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Crimp Seal MST | 214°F | untreated |
| 234°F | treated | |
| Crimp Seal Strength | 600 g/in | 250°F, 20psi, 3/4sec |
| Wetting Tension | 0.8 receding COS theta | Treated Surface |
| Yield | 24500 in2/lb |
Users viewing this material also viewed the following:
- Polyplastic TechnoTep B® 45 D Thermoplastic Elastomer, Mineral Filled
- Polykemi AB SCANTEC PC S75R GF20 V0 Polycarbonate, Glass Fiber Reinforced, Flame Retardant
- Menzolit Menzolit® BMC 0400 Unsaturated Polyester UP
- H.C. Starck Amperit® 832.054 Zirconium Oxide-Yttrium Oxide 93-7 (ZrO2-Y2O3)
- Ipiranga Petrochem PRA 0852 Polypropylene
- A. Schulman POLYFLAM™ FPP 1007 Talc Filled Homopolymer Polypropylene
- A. Schulman POLYBATCH™ ASP-2000 Permanent Antistatic Product
- Eagle Brass 110 EPT COPPER, 1/4 Hard
- Axiall 971 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved