DuPont Vamac® GXF Sample Compound Vulcanizate Slab Cure (5 minutes at 190°C)

Category	Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE)
Manufacturer	DuPont Packaging and Industrial Polymers
Trade Name	Vamac®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Vamac® GXF Sample Compound Vulcanizate Slab Cure (5 minutes at 190°C).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Test slab is cured for 5 minutes at 190°C and post cured for 4hrs at 175°C. Vulcanizate performance test data can help end-users evaluate the potential fitness of similar compounds for their own applications.Information provided by DuPont.

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	63	63
Tensile Strength, Ultimate	19.5 MPa	2830 psi
Elongation at Break	440 %	440 %
100% Modulus	0.00270 GPa	0.392 ksi
Tear Strength	21.5 kN/m	123 pli	ISO 34
Compression Set	27.3 %	27.3 %	70 hrs at 150°C

Descriptive Properties	Value	Comments
Armeen® 18D	0.5 parts
Diak No. 1	1.5 parts
DOTG Coaccelerator	4 parts
Naugard® 445 antioxidant	2 parts
SRF Black(N774)	45 parts
Stearic Acid	1.5 parts
Vamac® GXF	100 parts
Vanfre® VAM	1 part