DuPont Vamac® G/HVG Sample Compound (discontinued **)
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Vamac® G/HVG Sample Compound
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Test compound is press cured for 5 minutes at 175°C and post cured for 4 hours at 175°C.Information provided by DuPont.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 41 @Temperature 100 °C |
41 @Temperature 212 °F |
ML(1+4); ASTM D1646 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 64 | 64 | ASTM D2240 |
| Tensile Strength, Ultimate | 15.8 MPa | 2290 psi | ASTM D412 |
| Elongation at Break | 290 % | 290 % | ASTM D412 |
| 100% Modulus | 0.00570 GPa | 0.827 ksi | ASTM D412 |
| Compression Set | 18 % | 18 % | 70 hrs at 150°C; ASTM D395 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Armeen® 18D | 0.5 phr | |
| Diak No. 1 | 1.5 phr | |
| DOTG Coaccelerator | 4 phr | |
| Mooney Scorch at 121°C, Minimum Viscosity | 17.2 metric minutes | Mooney Units, ASTM D1646 |
| Mooney Scorch at 121°C, t10 | 12.7 metric minutes | Time for 10 unit rise, ASTM D1646 |
| Mooney Scorch at 121°C, t18 | >21 metric minutes | Time for 18 unit rise, ASTM D1646 |
| N550 Black | 60 phr | |
| Naugard® 445 antioxidant | 2 phr | |
| Stearic Acid | 1.5 phr | |
| TP-763 | 10 phr | |
| Vamac® G | 50 phr | |
| Vamac® HVG | 50 phr | |
| Vanfre® VAM | 1.5 phr |
Users viewing this material also viewed the following:
- SABIC PVC 70S Suspension Polyvinyl Chloride for Flexible Products
- SABIC Innovative Plastics Cycoloy® C6200 PC+ABS
- Gromax BFG45-AS00N1 Nylon 6 46% Glass Filled (Conditioned)
- Samsung Cheil Industries Starex® SG-401 Expandable Polystyrene (EPS) High Expansion
- Chase Plastics CP Pryme® N130GL (DAM) Nylon 6, 30% Glass Fiber Reinforced, Internally Lubricated
- A. Schulman VOLOY™ 462 Hybrid Reinforced PBT Alloy
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 400ºF Cure Temperature
- China-Yixing Longly Refractories Steatite Ceramics (High Frequency Porcelain)
- BASF Ultramid® A3WG3 BK 00564 15% Glass Filled PA66 (Dry)
- Radici Heraform® R 1300 Acetal Copolymer
Copyright © lookpolymers.com All Rights Reserved