DuPont Teijin Films Mylar® A Polyester Film, 92 Gauge

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Mylar®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Mylar® A Polyester Film, 92 Gauge.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Mylar® A films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion, and processability.Mylar® A films have balanced tensile properties and excellent resistance to moisture and most chemicals. They can withstand temperature extremes from -100°F to 300ºF. Mylar® does not become brittle with age under normal conditions, because it contains no plasticizers. Typical Applications:Apparel staysBook jacketsCarbon ribbonControl TapeDrumheadsDuct LinersIdentificationsMembrane touch switchesMetallized BasePressure Sensitive Labels (plain or metallized)Protective surfacingRelease linersRoll leaf (hot stamping)Spirit MastersApprovals: FDA Food Contact Status - All gauges of Mylar® A comply with the Food and Drug Administration regulation 21 CFR 177.1630 -- Polyethylene phthalate polymers. This regulation describes films which may be safely used in contact with all types of food excluding alcoholic beverages. Uncoated films such as Mylar® A can be used to contain foods during oven cooking or oven baking at temperatures above 250 °F. UL 94 VTM-2 - for 92-1400 gauge (0.023 - 0.35mm). UL Recognition - for 92-500 gauge (0.023-0.13mm) HWI=5, HAI=4, CTI=1; for 700-1400 gauge (0.18-0.35mm) HWI=4, HAI=0, CTI=1Information provided by DuPont.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ASTM D1505
Viscosity Measurement 0.56
0.56
ASTM D2857
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 103 MPa

@Strain 5.00 %
15000 psi

@Strain 5.00 %
ASTM D882
Film Tensile Strength at Yield, TD 96.5 MPa

@Strain 5.00 %
14000 psi

@Strain 5.00 %
ASTM D882
Film Elongation at Break, MD 110 %
110 %
ASTM D882A
Film Elongation at Break, TD 90 %
90 %
ASTM D882A
Tensile Modulus 3.50 GPa
507 ksi
ASTM D822
Poissons Ratio 0.38
0.38
Typical Mylar® before yield
0.58
0.58
Typical Mylar® after yield
Film Tensile Strength at Break, MD 193 MPa
28000 psi
ASTM D882A
Film Tensile Strength at Break, TD 234 MPa
34000 psi
ASTM D882A
Thermal Properties Metric English Comments
CTE, linear 17.0 µm/m-°C

@Temperature 30.0 - 50.0 °C
9.44 µin/in-°F

@Temperature 86.0 - 122 °F
92 Gauge; ASTM D696
Specific Heat Capacity 1.17 J/g-°C
0.280 BTU/lb-°F
Thermal Conductivity 0.155 W/m-K

@Temperature 25.0 - 75.0 °C
1.07 BTU-in/hr-ft²-°F

@Temperature 77.0 - 167 °F
(Mylar® 1000A)
Melting Point 254 °C
489 °F
DSC
Maximum Service Temperature, Air 149 °C
300 °F
Maximum Service Temperature, Inert -73.3 °C
-100 °F
Shrinkage, MD 1.9 %

@Temperature 150 °C,
Time 1800 sec
1.9 %

@Temperature 302 °F,
Time 0.500 hour
Unrestrained
Shrinkage, TD 1.1 %

@Temperature 150 °C,
Time 1800 sec
1.1 %

@Temperature 302 °F,
Time 0.500 hour
Unrestrained
Optical Properties Metric English Comments
Refractive Index 1.64 - 1.67
1.64 - 1.67
typical of Mylar®
Haze 16 %
16 %
ASTM D1003
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Electrical Properties Metric English Comments
Comparative Tracking Index 400 - 600 V
400 - 600 V
Hot Wire Ignition, HWI <= 7.0 sec
<= 7.0 sec
High Amp Arc Ignition, HAI <= 15 arcs
<= 15 arcs
Descriptive Properties Value Comments
Yield (nominal) 21500 in2/lb