DuPont Teijin Films Melinex® 314 Polyester Film, 92 Gauge
| Category | Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film |
| Manufacturer | DuPont Teijin Films (DTF) |
| Trade Name | Melinex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Teijin Films Melinex® 314 Polyester Film, 92 Gauge.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Melinex® 314 is a two-side adhesion promoting polyester film with consistently good handling properties.Information provided by DuPont.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 100 MPa | 14500 psi | ASTM D882A |
| Film Tensile Strength at Yield, TD | 99.3 MPa | 14400 psi | ASTM D882A |
| Film Elongation at Break, MD | 150 % | 150 % | ASTM D882A |
| Film Elongation at Break, TD | 100 % | 100 % | ASTM D882A |
| Coefficient of Friction, Dynamic | 0.40 @Thickness 0.0234 mm |
0.40 @Thickness 0.000920 in |
A-B; ASTM D1894 |
| Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
| Film Tensile Strength at Break, TD | 248 MPa | 36000 psi | ASTM D882A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 3.5 % @Temperature 190 °C, Time 300 sec |
3.5 % @Temperature 374 °F, Time 0.0833 hour |
Unrestrained |
| Shrinkage, TD | 3.5 % @Temperature 190 °C, Time 300 sec |
3.5 % @Temperature 374 °F, Time 0.0833 hour |
Unrestrained |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 5.6 % @Thickness 0.0234 mm |
5.6 % @Thickness 0.000920 in |
ASTM D1003 |
| Transmission, Visible | 87 % @Thickness 0.0234 mm |
87 % @Thickness 0.000920 in |
TLT; ASTM D1003 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible R276AE Polyvinyl Chloride, Flexible (PVC, Flexible)
- Lehmann & Voss LUVOCOM® 1105-7185 PEEK, with carbon fiber, PTFE, lubricant modified
- Inno-Comp INNOPOL® CS 2-4630 GFR Flame Retarded Polypropylene Block-Copolymer
- Solvay Specialty Polymers Ajedium™ Films -- Udel® PSU P-1700 NT-11 Polysulfone (PSU)
- Solvay ANTAROX® V 27 Surfactant
- A. Schulman ComAlloy® E-13819 Heat Dissipative PPS
- Denka REOMER G G5379 Thermoplastic Elastomer, For Extrusion
- Braskem CN8092 EVA Molding Copolymer
- Asahi Kasei Leona® 1300G Polyamide 66 Resin, Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved