DuPont Performance Polymers Zytel® 70G20HSL NC010 Nylon 66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 70G20HSL NC010 Nylon 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
DAM; ISO 1183
Water Absorption 2.1 %

@Temperature 23.0 °C
 2.1 %

@Temperature 73.4 °F
 Equilibrium 50%RH; DAM; ISO 62, Similar to
6.8 %

@Temperature 23.0 °C
 6.8 %

@Temperature 73.4 °F
 Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Thickness 2.00 mm
 0.0040 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.012 cm/cm

@Thickness 2.00 mm
 0.012 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 85
85
50%RH; ISO 2039/2
102
102
DAM; ISO 2039/2
Hardness, Rockwell R 115
115
50%RH; ISO 2039/2
122
122
DAM; ISO 2039/2
Tensile Strength at Break 103 MPa

@Temperature 23.0 °C
 14900 psi

@Temperature 73.4 °F
 50%RH; ISO 527
159 MPa

@Temperature 23.0 °C
 23100 psi

@Temperature 73.4 °F
 DAM; ISO 527
Tensile Stress 17.5 MPa

@Strain 0.530 %,
Temperature 120 °C
 2540 psi

@Strain 0.530 %,
Temperature 248 °F
 50%RH; ISO 527
18.5 MPa

@Strain 0.520 %,
Temperature 90.0 °C
 2680 psi

@Strain 0.520 %,
Temperature 194 °F
 50%RH; ISO 527
20.5 MPa

@Strain 0.520 %,
Temperature 60.0 °C
 2970 psi

@Strain 0.520 %,
Temperature 140 °F
 50%RH; ISO 527
22.2 MPa

@Strain 0.630 %,
Temperature 120 °C
 3220 psi

@Strain 0.630 %,
Temperature 248 °F
 DAM; ISO 527
23.0 MPa

@Strain 0.480 %,
Temperature 40.0 °C
 3340 psi

@Strain 0.480 %,
Temperature 104 °F
 50%RH; ISO 527
24.5 MPa

@Strain 0.610 %,
Temperature 90.0 °C
 3550 psi

@Strain 0.610 %,
Temperature 194 °F
 DAM; ISO 527
25.9 MPa

@Strain 0.440 %,
Temperature 23.0 °C
 3760 psi

@Strain 0.440 %,
Temperature 73.4 °F
 50%RH; ISO 527
26.2 MPa

@Strain 0.460 %,
Temperature 60.0 °C
 3800 psi

@Strain 0.460 %,
Temperature 140 °F
 DAM; ISO 527
27.7 MPa

@Strain 0.270 %,
Temperature -20.0 °C
 4020 psi

@Strain 0.270 %,
Temperature -4.00 °F
 50%RH; ISO 527
28.8 MPa

@Strain 0.330 %,
Temperature 0.000 °C
 4180 psi

@Strain 0.330 %,
Temperature 32.0 °F
 50%RH; ISO 527
30.6 MPa

@Strain 1.06 %,
Temperature 120 °C
 4440 psi

@Strain 1.06 %,
Temperature 248 °F
 50%RH; ISO 527
33.2 MPa

@Strain 0.360 %,
Temperature 40.0 °C
 4820 psi

@Strain 0.360 %,
Temperature 104 °F
 DAM; ISO 527
33.4 MPa

@Strain 1.04 %,
Temperature 90.0 °C
 4840 psi

@Strain 1.04 %,
Temperature 194 °F
 50%RH; ISO 527
35.9 MPa

@Strain 0.250 %,
Temperature 23.0 °C
 5210 psi

@Strain 0.250 %,
Temperature 73.4 °F
 DAM; ISO 527
37.4 MPa

@Strain 1.04 %,
Temperature 60.0 °C
 5420 psi

@Strain 1.04 %,
Temperature 140 °F
 50%RH; ISO 527
38.3 MPa

@Strain 1.26 %,
Temperature 120 °C
 5550 psi

@Strain 1.26 %,
Temperature 248 °F
 DAM; ISO 527
40.4 MPa

@Strain 1.59 %,
Temperature 120 °C
 5860 psi

@Strain 1.59 %,
Temperature 248 °F
 50%RH; ISO 527
41.2 MPa

@Strain 0.960 %,
Temperature 40.0 °C
 5980 psi

@Strain 0.960 %,
Temperature 104 °F
 50%RH; ISO 527
42.0 MPa

@Strain 1.22 %,
Temperature 90.0 °C
 6090 psi

@Strain 1.22 %,
Temperature 194 °F
 DAM; ISO 527
45.1 MPa

@Strain 1.56 %,
Temperature 90.0 °C
 6540 psi

@Strain 1.56 %,
Temperature 194 °F
 50%RH; ISO 527
45.4 MPa

@Strain 0.920 %,
Temperature 60.0 °C
 6580 psi

@Strain 0.920 %,
Temperature 140 °F
 DAM; ISO 527
46.8 MPa

@Strain 0.880 %,
Temperature 23.0 °C
 6790 psi

@Strain 0.880 %,
Temperature 73.4 °F
 50%RH; ISO 527
47.6 MPa

@Strain 2.12 %,
Temperature 120 °C
 6900 psi

@Strain 2.12 %,
Temperature 248 °F
 50%RH; ISO 527
50.2 MPa

@Strain 1.89 %,
Temperature 120 °C
 7280 psi

@Strain 1.89 %,
Temperature 248 °F
 DAM; ISO 527
50.7 MPa

@Strain 1.56 %,
Temperature 60.0 °C
 7350 psi

@Strain 1.56 %,
Temperature 140 °F
 50%RH; ISO 527
51.2 MPa

@Strain 0.540 %,
Temperature -20.0 °C
 7430 psi

@Strain 0.540 %,
Temperature -4.00 °F
 50%RH; ISO 527
52.4 MPa

@Strain 0.660 %,
Temperature 0.000 °C
 7600 psi

@Strain 0.660 %,
Temperature 32.0 °F
 50%RH; ISO 527
52.8 MPa

@Strain 2.65 %,
Temperature 120 °C
 7660 psi

@Strain 2.65 %,
Temperature 248 °F
 50%RH; ISO 527
53.9 MPa

@Strain 2.08 %,
Temperature 90.0 °C
 7820 psi

@Strain 2.08 %,
Temperature 194 °F
 50%RH; ISO 527
55.4 MPa

@Strain 1.44 %,
Temperature 40.0 °C
 8040 psi

@Strain 1.44 %,
Temperature 104 °F
 50%RH; ISO 527
55.7 MPa

@Strain 1.83 %,
Temperature 90.0 °C
 8080 psi

@Strain 1.83 %,
Temperature 194 °F
 DAM; ISO 527
56.5 MPa

@Strain 3.18 %,
Temperature 120 °C
 8190 psi

@Strain 3.18 %,
Temperature 248 °F
 50%RH; ISO 527
57.7 MPa

@Strain 0.720 %,
Temperature 40.0 °C
 8370 psi

@Strain 0.720 %,
Temperature 104 °F
 DAM; ISO 527
58.8 MPa

@Strain 2.52 %,
Temperature 120 °C
 8530 psi

@Strain 2.52 %,
Temperature 248 °F
 DAM; ISO 527
59.0 MPa

@Strain 3.71 %,
Temperature 120 °C
 8560 psi

@Strain 3.71 %,
Temperature 248 °F
 50%RH; ISO 527
60.0 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 8700 psi

@Strain 0.500 %,
Temperature 73.4 °F
 DAM; ISO 527
60.4 MPa

@Strain 2.60 %,
Temperature 90.0 °C
 8760 psi

@Strain 2.60 %,
Temperature 194 °F
 50%RH; ISO 527
60.7 MPa

@Strain 4.24 %,
Temperature 120 °C
 8800 psi

@Strain 4.24 %,
Temperature 248 °F
 50%RH; ISO 527
61.0 MPa

@Strain 1.38 %,
Temperature 60.0 °C
 8850 psi

@Strain 1.38 %,
Temperature 140 °F
 DAM; ISO 527
61.1 MPa

@Strain 2.08 %,
Temperature 60.0 °C
 8860 psi

@Strain 2.08 %,
Temperature 140 °F
 50%RH; ISO 527
61.7 MPa

@Strain 4.77 %,
Temperature 120 °C
 8950 psi

@Strain 4.77 %,
Temperature 248 °F
 50%RH; ISO 527
62.2 MPa

@Strain 5.30 %,
Temperature 120 °C
 9020 psi

@Strain 5.30 %,
Temperature 248 °F
 50%RH; Break; ISO 527
63.2 MPa

@Strain 1.32 %,
Temperature 23.0 °C
 9170 psi

@Strain 1.32 %,
Temperature 73.4 °F
 50%RH; ISO 527
64.5 MPa

@Strain 3.15 %,
Temperature 120 °C
 9350 psi

@Strain 3.15 %,
Temperature 248 °F
 DAM; ISO 527
65.1 MPa

@Strain 3.12 %,
Temperature 90.0 °C
 9440 psi

@Strain 3.12 %,
Temperature 194 °F
 50%RH; ISO 527
66.0 MPa

@Strain 2.44 %,
Temperature 90.0 °C
 9570 psi

@Strain 2.44 %,
Temperature 194 °F
 DAM; ISO 527
66.4 MPa

@Strain 1.92 %,
Temperature 40.0 °C
 9630 psi

@Strain 1.92 %,
Temperature 104 °F
 50%RH; ISO 527
68.1 MPa

@Strain 3.78 %,
Temperature 120 °C
 9880 psi

@Strain 3.78 %,
Temperature 248 °F
 DAM; ISO 527
68.2 MPa

@Strain 3.64 %,
Temperature 90.0 °C
 9890 psi

@Strain 3.64 %,
Temperature 194 °F
 50%RH; ISO 527
68.8 MPa

@Strain 2.60 %,
Temperature 60.0 °C
 9980 psi

@Strain 2.60 %,
Temperature 140 °F
 50%RH; ISO 527
70.1 MPa

@Strain 4.41 %,
Temperature 120 °C
 10200 psi

@Strain 4.41 %,
Temperature 248 °F
 DAM; ISO 527
70.3 MPa

@Strain 4.16 %,
Temperature 90.0 °C
 10200 psi

@Strain 4.16 %,
Temperature 194 °F
 50%RH; ISO 527
71.3 MPa

@Strain 5.04 %,
Temperature 120 °C
 10300 psi

@Strain 5.04 %,
Temperature 248 °F
 DAM; ISO 527
71.4 MPa

@Strain 4.68 %,
Temperature 90.0 °C
 10400 psi

@Strain 4.68 %,
Temperature 194 °F
 50%RH; ISO 527
71.4 MPa

@Strain 0.810 %,
Temperature -20.0 °C
 10400 psi

@Strain 0.810 %,
Temperature -4.00 °F
 50%RH; ISO 527