- DuPont Performance Polymers VTR 8500 (GLT-S) 8500 Peroxide Cured Fluoroelastomer (FKM) Formulation (discontin
DuPont Performance Polymers VTR 8500 (GLT-S) 8500 Peroxide Cured Fluoroelastomer (FKM) Formulation (discontin
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers VTR 8500 (GLT-S) 8500 Peroxide Cured Fluoroelastomer (FKM) Formulation
(discontin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationViton® GLT
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 66 @Temperature 121 °C |
66 @Temperature 250 °F |
ML-10 (gum)-Akron data |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 67 | 67 | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Tensile Strength, Ultimate | 17.8 MPa | 2580 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Elongation at Break | 267 % | 267 % | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Modulus of Elasticity | 0.000600 GPa | 0.0870 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| 100% Modulus | 0.00360 GPa | 0.522 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Compression Set | 11 % @Temperature 200 °C |
11 % @Temperature 392 °F |
Method B, O-rings 22 hr at 200°C (Cured 7 min at 177°C and Post Cured 2 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -31.4 °C | -24.5 °F | TR-10 |
| Glass Transition Temp, Tg | -32.9 °C | -27.2 °F | DSC |
Users viewing this material also viewed the following:
- LyondellBasell Lupolen® 5261 ZS HDPE, Blow Molding Grade
- Kazanorgsintez M 168 Polymer Composition for Rotary Molding
- LyondellBasell Pro-fax SR549M Polypropylene Random Copolymer, Clarified
- Shin-Etsu Silicones KF-6012 Fluid
- Teknor Apex Sarlink® 3460 Thermoplastic Elastomer
- Wellman Wellamid® MRGF25/15 42H-GY1 40% Mineral/Glass Fiber Reinforced Nylon 6
- CIMBAR Gel Talc for Polyester Filler
- Dow SiLK™ I300 280 Semiconductor Dielectric Resin
- 3M 6035PC 12036 Polyurethane Foam Tape (15 lb./ft3 (239 kg/m3) Series)
Copyright © lookpolymers.com All Rights Reserved