DuPont Performance Polymers Hytrel® 3078 Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® 3078 Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30 Shore D High Performance Polyester Elastomer with Non-discoloring Stabilizer Hytrel 3078 is a very low modulus grade with nominal hardness of 30D. It contains non-discoloring stabilizer. It can be processed by many conventional thermoplastic processInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 0.940 g/cc
0.0340 lb/in³
1.07 g/cc
0.0387 lb/in³
ISO 1183
Water Absorption 0.80 %

@Thickness 2.00 mm
 0.80 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Water Absorption at Saturation 0.50 %
0.50 %
Immersion 24h; ASTM D570
Viscosity 80430 cP

@Shear Rate 5000 1/s,
Temperature 215 °C
 80430 cP

@Shear Rate 5000 1/s,
Temperature 419 °F
 ISO 11403-1 -2
84630 cP

@Shear Rate 5000 1/s,
Temperature 205 °C
 84630 cP

@Shear Rate 5000 1/s,
Temperature 401 °F
 ISO 11403-1 -2
91640 cP

@Shear Rate 5000 1/s,
Temperature 190 °C
 91640 cP

@Shear Rate 5000 1/s,
Temperature 374 °F
 ISO 11403-1 -2
309800 cP

@Shear Rate 500 1/s,
Temperature 215 °C
 309800 cP

@Shear Rate 500 1/s,
Temperature 419 °F
 ISO 11403-1 -2
340200 cP

@Shear Rate 500 1/s,
Temperature 205 °C
 340200 cP

@Shear Rate 500 1/s,
Temperature 401 °F
 ISO 11403-1 -2
391600 cP

@Shear Rate 500 1/s,
Temperature 190 °C
 391600 cP

@Shear Rate 500 1/s,
Temperature 374 °F
 ISO 11403-1 -2
569300 cP

@Shear Rate 10.0 1/s,
Temperature 215 °C
 569300 cP

@Shear Rate 10.0 1/s,
Temperature 419 °F
 ISO 11403-1 -2
670400 cP

@Shear Rate 10.0 1/s,
Temperature 205 °C
 670400 cP

@Shear Rate 10.0 1/s,
Temperature 401 °F
 ISO 11403-1 -2
871300 cP

@Shear Rate 10.0 1/s,
Temperature 190 °C
 871300 cP

@Shear Rate 10.0 1/s,
Temperature 374 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.0060 cm/cm
0.0060 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ISO 294-4 2577
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 5.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm³/10min; ISO 1133
5.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 5.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 26
26
15s; ISO 868
<= 30
<= 30
ISO 868
Tensile Strength at Break 24.0 MPa
3480 psi
ISO 527-1/-2
Tensile Stress 1.80 MPa

@Strain 10.0 %
 261 psi

@Strain 10.0 %
 ISO 527-1/-2
5.00 MPa

@Strain 50.0 %
 725 psi

@Strain 50.0 %
 ISO 527-1/-2
0.620 MPa

@Strain 7.80 %,
Temperature 120 °C
 89.9 psi

@Strain 7.80 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
0.890 MPa

@Strain 7.88 %,
Temperature 100 °C
 129 psi

@Strain 7.88 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
0.960 MPa

@Strain 18.94 %,
Temperature 120 °C
 139 psi

@Strain 18.94 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.04 MPa

@Strain 7.84 %,
Temperature 90.0 °C
 151 psi

@Strain 7.84 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
1.13 MPa

@Strain 30.07 %,
Temperature 120 °C
 164 psi

@Strain 30.07 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.24 MPa

@Strain 41.21 %,
Temperature 120 °C
 180 psi

@Strain 41.21 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.27 MPa

@Strain 7.29 %,
Temperature 60.0 °C
 184 psi

@Strain 7.29 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
1.31 MPa

@Strain 52.35 %,
Temperature 120 °C
 190 psi

@Strain 52.35 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.36 MPa

@Strain 6.64 %,
Temperature 40.0 °C
 197 psi

@Strain 6.64 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
1.37 MPa

@Strain 5.71 %,
Temperature 0.000 °C
 199 psi

@Strain 5.71 %,
Temperature 32.0 °F
 TPE; ISO 11403-1 -2
1.37 MPa

@Strain 67.2 %,
Temperature 120 °C
 199 psi

@Strain 67.2 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.40 MPa

@Strain 82.8 %,
Temperature 120 °C
 203 psi

@Strain 82.8 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.40 MPa

@Strain 149.63 %,
Temperature 120 °C
 203 psi

@Strain 149.63 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.40 MPa

@Strain 168.19 %,
Temperature 120 °C
 203 psi

@Strain 168.19 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.41 MPa

@Strain 19.13 %,
Temperature 100 °C
 205 psi

@Strain 19.13 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
1.42 MPa

@Strain 134.78 %,
Temperature 120 °C
 206 psi

@Strain 134.78 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.45 MPa

@Strain 97.65 %,
Temperature 120 °C
 210 psi

@Strain 97.65 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.45 MPa

@Strain 112.5 %,
Temperature 120 °C
 210 psi

@Strain 112.5 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.64 MPa

@Strain 18.07 %,
Temperature 90.0 °C
 238 psi

@Strain 18.07 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
1.68 MPa

@Strain 30.38 %,
Temperature 100 °C
 244 psi

@Strain 30.38 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
1.74 MPa

@Strain 8.52 %,
Temperature 23.0 °C
 252 psi

@Strain 8.52 %,
Temperature 73.4 °F
 TPE; ISO 11403-1 -2
1.80 MPa

@Strain 10.0 %,
Temperature 23.0 °C
 261 psi

@Strain 10.0 %,
Temperature 73.4 °F
 ISO 11403-1 -2
1.83 MPa

@Strain 41.63 %,
Temperature 100 °C
 265 psi

@Strain 41.63 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
1.94 MPa

@Strain 52.88 %,
Temperature 100 °C
 281 psi

@Strain 52.88 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
1.98 MPa

@Strain 28.98 %,
Temperature 90.0 °C
 287 psi

@Strain 28.98 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
2.03 MPa

@Strain 67.88 %,
Temperature 100 °C
 294 psi

@Strain 67.88 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
2.08 MPa

@Strain 17.02 %,
Temperature 60.0 °C
 302 psi

@Strain 17.02 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
2.09 MPa

@Strain 82.14 %,
Temperature 100 °C
 303 psi

@Strain 82.14 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
2.14 MPa

@Strain 97.14 %,
Temperature 100 °C
 310 psi

@Strain 97.14 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
2.18 MPa

@Strain 112.14 %,
Temperature 100 °C
 316 psi

@Strain 112.14 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
2.18 MPa

@Strain 39.89 %,
Temperature 90.0 °C
 316 psi

@Strain 39.89 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
2.25 MPa

@Strain 134.64 %,
Temperature 100 °C
 326 psi

@Strain 134.64 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
2.28 MPa

@Strain 149.65 %,
Temperature 100 °C
 331 psi

@Strain 149.65 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
2.32 MPa

@Strain 168.4 %,
Temperature 100 °C
 336 psi

@Strain 168.4 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
2.33 MPa

@Strain 50.8 %,
Temperature 90.0 °C
 338 psi

@Strain 50.8 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
2.34 MPa

@Strain 16.44 %,
Temperature 40.0 °C
 339 psi

@Strain 16.44 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
2.41 MPa

@Strain 65.12 %,
Temperature 90.0 °C
 350 psi

@Strain 65.12 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
2.43 MPa

@Strain 13.11 %,
Temperature 0.000 °C
 352 psi

@Strain 13.11 %,
Temperature 32.0 °F
 TPE; ISO 11403-1 -2
2.49 MPa

@Strain 79.43 %,
Temperature 90.0 °C
 361 psi

@Strain 79.43 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
2.55 MPa

@Strain 93.75 %,
Temperature 90.0 °C
 370 psi

@Strain 93.75 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
2.55 MPa

@Strain 26.74 %,
Temperature 60.0 °C
 370 psi

@Strain 26.74 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
2.59 MPa

@Strain 5.25 %,
Temperature -20.0 °C
 376 psi

@Strain 5.25 %,
Temperature -4.00 °F
 TPE; ISO 11403-1 -2