DuPont Performance Polymers Delrin® 911DP NC010 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 911DP NC010 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nucleated Low Viscosity Acetal Homopolymer Delrin 911DP is a low viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage less shrinkage fewer voids).Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 0.90 %

@Thickness 2.00 mm
0.90 %

@Thickness 0.0787 in
Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
0.200 %

@Thickness 0.0787 in
Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.019 cm/cm
0.019 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.018 cm/cm
0.018 in/in
ISO 294-4 2577
Melt Flow 21 g/10 min

@Load 2.16 kg,
Temperature 190 °C
21 g/10 min

@Load 4.76 lb,
Temperature 374 °F
cm³/10min; ISO 1133
24 g/10 min

@Load 2.16 kg,
Temperature 190 °C
24 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 75.0 MPa
10900 psi
ISO 527-1/-2
Elongation at Break 20 %
20 %
Nominal; ISO 527-1/-2
Elongation at Yield 10 %
10 %
ISO 527-1/-2
Tensile Modulus 3.40 GPa
493 ksi
ISO 527-1/-2
Flexural Strength 90.0 MPa

@Strain 3.50 %
13100 psi

@Strain 3.50 %
ISO 178
Flexural Modulus 3.30 GPa
479 ksi
ISO 178
Charpy Impact Unnotched 16.0 J/cm²
76.1 ft-lb/in²
ISO 179/1eU
15.0 J/cm²

@Temperature -30.0 °C
71.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.650 J/cm²
3.09 ft-lb/in²
ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 163 °C
325 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 108 °C
226 °F
ISO 75-1/-2
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Part Marking Code >POM<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification POM
ISO 1043
Copyright © lookpolymers.com All Rights Reserved