DuPont™ Clysar® EHC Polyolefin Shrink Packaging Film, 100 Gauge (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , Polyolefin , Polyolefin, Film Grade , Polyolefin, Film Grade (Polyolefin) , Polypropylene (PP)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont™ Clysar® EHC Polyolefin Shrink Packaging Film, 100 Gauge (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by DuPont Packaging Polymers.A biaxially oriented, heat-shrinkable copolymer film. It is a polypropylene and polyethylene-based film that is predominantly polypropylene. Used when excellent optics, high shrink force, and superb sheet flatness are essential. An excellent choice for doing multi-packs, high-speed applications, and static sealing.

Physical Properties	Metric	English	Comments
Oxygen Transmission	103 cc-mm/m²-24hr-atm	262 cc-mil/100 in²-24hr-atm	or 4100 cc/m²-24hr-atm for the film. ASTM D3985

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	130 %	130 %	Average; ASTM D882
Modulus of Elasticity	0.770 GPa	112 ksi	(stiffness), ASTM D882
Coefficient of Friction, Dynamic	0.40	0.40	ASTM D1894
Elmendorf Tear Strength MD	7.0 g	7.0 g	Orientation not specified; ASTM D1922
Seal Strength	3200 g/25 mm	3200 g/in	F-88-68(73)
Film Tensile Strength at Break, MD	131 MPa	19000 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	1.2 %	1.2 %
Gloss	125 %	125 %

Processing Properties	Metric	English	Comments
Processing Temperature	177 - 232 °C	351 - 450 °F	Optimum Tunnel temperature range.