Dow Nordel® IP 4770P Dense Extruded Profile
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Dow Chemical |
| Trade Name | Nordel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Nordel® IP 4770P Dense Extruded Profile.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationNordel® IP 4770P
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.185 g/cc | 0.04281 lb/in³ | |
| Mooney Viscosity | 47 @Temperature 100 °C |
47 @Temperature 212 °F |
ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 10.4 MPa | 1510 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 446 % | 446 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00380 GPa | 0.551 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00750 GPa | 1.09 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.00900 GPa | 1.31 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 88 % @Temperature 125 °C |
88 % @Temperature 257 °F |
Pellets cured MDR TC95 + 15 min, 70 hr; Method B |
Users viewing this material also viewed the following:
- Quadrant EPP Techtron® HPV PPS (ASTM Product Data Sheet)
- Polymer Resources TP-FR IM2 PBT, Impact Modified, Flame Retardant, High Flow
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR Mistron Vapor Filler
- SABIC Innovative Plastics LNP LUBRICOMP NXCY620 PC+ABS
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 5 PHR Di-Cup 40C
- BNZ Materials BNZP-23 Insulating Firebrick (French Grade)
- Arkema Group Rilsan® AZM 30 O TLD Nylon 12, 30% Glass Fiber Filled (Conditioned)
Copyright © lookpolymers.com All Rights Reserved