Dow Elite® 5100 Linear Low Density Polyethylene

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer Dow Chemical
Trade Name Elite®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow Elite® 5100 Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
5100 enhanced polyethylene resin is a copolymer produced via INSITE Technology from Dow Plastics. It offers extremely high impact resistance, combined with excellent tear, tensile, and puncture properties for thick and thin gauge industrial and consumer blown film applications. 5100 resin exhibits a broader range and higher hot tack strengths than LLDPE, making it ideal for automated packaging applications. It complies with U.S. FDA regulation 21 CFR 177.1520 c 3.2 (a) when used unmodified and processed according to good manufacturing practices. For food contact compliance statements, your nearest Dow office should be contacted.Data provided by Dow Chemical.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
Melt Flow 0.85 g/10 min

@Load 2.16 kg
0.85 g/10 min

@Load 4.76 lb
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.4 MPa
1650 psi
Film Tensile Strength at Yield, TD 11.5 MPa
1670 psi
Film Elongation at Break, MD 645 %
645 %
Film Elongation at Break, TD 655 %
655 %
Secant Modulus, MD 0.200 GPa
29.0 ksi
Film value
Secant Modulus, TD 0.217 GPa
31.5 ksi
Film value
Elmendorf Tear Strength MD 907 g
907 g
Unspecified film thickness
Elmendorf Tear Strength TD 1110 g
1110 g
Unspecified film thickness
Dart Drop Test >= 830 g
>= 1.83 lb
Film Tensile Strength at Break, MD 56.3 MPa
8170 psi
Film Tensile Strength at Break, TD 44.2 MPa
6410 psi
Thermal Properties Metric English Comments
Vicat Softening Point 107 °C
225 °F
Optical Properties Metric English Comments
Haze 11 %
11 %
Processing Properties Metric English Comments
Processing Temperature 101 °C
214 °F
Seal Initiation temperature