Dow DNDA-8335 NT 7 Linear Low Density Polyethylene Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | Dow Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DNDA-8335 NT 7 Linear Low Density Polyethylene Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DOW DNDA-8335 NT 7 is produced using UNIPOL™ PE process technology. It is intended for use in general purpose injection molding applications. Information provided by Dow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ASTM D792 |
| ESCR 100% Igepal® | 10 hour @Temperature 50.0 °C |
10 hour @Temperature 122 °F |
F<sub>50</sub>; Molded and tested in accordance with ASTM D4976; ASTM D1693 |
| Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 190 °C |
35 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 51 | 51 | Molded and tested in accordance with ASTM D4976; ASTM D2240 |
| Tensile Strength at Break | 7.58 MPa | 1100 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 75 % | 75 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 0.393 GPa | 57.0 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
| Tensile Impact Strength | 189 kJ/m² | 90.0 ft-lb/in² | Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) |
| Crystallization Temperature | 108 °C | 226 °F | Dow Method (DSC) |
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Vicat Softening Point | 92.2 °C | 198 °F | ASTM D1525 |
| Brittleness Temperature | -76.1 °C | -105 °F | Molded and tested in accordance with ASTM D4976; ASTM D746 |
Users viewing this material also viewed the following:
- Palm Labs Adhesives Turbo Fuse Series 140 (200 Viscosity) Rapid Bonding Adhesive
- Fujipoly Industries Sarcon® GR-Fd Gap Filler Pad
- McDanel Advanced Ceramics MV-20 Mullite
- Heraeus Cleviosâ„¢ PH Conductive Sulfonate Polymer for Antistatic Coatings
- SABIC Innovative Plastics LNP Thermocomp MB008S PP (Asia Pacific)
- Sax Polymers SAXALEN PPH305G30 Polypropylene Homopolymer, 30% Glass Filled
- Teknor Apex TEKBOND® 6000-60 Thermoplastic Elastomer
- Plastcom SLOVAMID 6 LI LS PA6, improved strength, light stability
Copyright © lookpolymers.com All Rights Reserved