Diamond Polymers ABSPC 7801E ABS/PC Extrusion Grade, High Impact, High Heat
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABSPC 7801E ABS/PC Extrusion Grade, High Impact, High Heat.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | chs 2.0 in/min; ASTM D638 |
| Tensile Modulus | 2.322 GPa | 336.8 ksi | chs 2.0 in/min; ASTM D638 |
| Flexural Strength | 66.0 MPa @Thickness 3.17 mm |
9570 psi @Thickness 0.125 in |
5% strain; chs 0.05 in/min; ASTM D790 |
| Flexural Modulus | 2.019 GPa @Thickness 3.17 mm |
292.8 ksi @Thickness 0.125 in |
tangent; chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 5.50 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
10.3 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 137 °C @Load 1.00 kg |
279 °F @Load 2.20 lb |
120°C/hr; ASTM D1525 |
Users viewing this material also viewed the following:
- Polimersan Plastics POLIPOM® (POM)
- PSM Industries PM Krupp M3/2 Powder Metallurgy Steel Alloy
- Garlock 3205 Neoprene/Polyester Fabric
- LG Chemical Lutex 120 NBR Latex
- Styron XZ 97217.00 Styrene Acrylate
- A. Schulman FORMION™ FI 225 30% Glass Fiber Reinforced Ionomer / Nylon Alloy
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N339 Filler
- EMS-Grivory Grivory® HTV-3H1 nat PA6T/6I-GF30
- Fainplast Compounds EVAtech 805S Ethylene Vinyl Acetate Foam
- Solvay TECHNYL® A 218 V35 Black 21NHFE PA66, 35% glass fiber, DRY
Copyright © lookpolymers.com All Rights Reserved