Daikin DAI-EL G-575 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 70% Fluorine Content

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Daikin Industries
Trade Name DAI-EL
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Daikin DAI-EL G-575 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 70% Fluorine Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Offers minimal compression set and excellent sealing. The terpolymer type is able to withstand polarized solvents to realize a wide range of application.Features: Low permeability to gasoline and alcohol mixed fuel oil and good extrudability.Information provided by Daikin Industries.
Physical Properties Metric English Comments
Specific Gravity 1.91 g/cc
1.91 g/cc
at 25°C
Mooney Viscosity 36

@Temperature 121 °C
36

@Temperature 250 °F
ML 1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 73
73
Peak value, at 25°C
Tensile Strength at Break 12.9 MPa
1870 psi
Tensile Strength, Yield 4.10 MPa

@Strain 100 %
595 psi

@Strain 100 %
Elongation at Break 290 %
290 %
Tear Strength 19.8 kN/m
113 pli
at 25°C
Compression Set 32 %
32 %
70 hours at 25°C
24 %

@Temperature 100 °C
24 %

@Temperature 212 °F
70 hours
28 %

@Temperature 175 °C
28 %

@Temperature 347 °F
70 hours
44 %

@Temperature 200 °C
44 %

@Temperature 392 °F
70 hours
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -11.0 °C
12.2 °F
TR test, TR10
-9.00 °C
15.8 °F
Gehman torsion test, T10
-5.00 °C
23.0 °F
TR test, TR70
-2.50 °C
27.5 °F
Gehman torsion test, T2
Brittleness Temperature -18.0 °C
-0.400 °F
Processing Properties Metric English Comments
Processing Temperature 160 °C
320 °F
Cure Measuring Temperature
Cure Time 6.70 min
0.112 hour
Curelastmeter