- Daelim H&L Plavis N Aromatic Polyimide, Non-Filled, Machined Parts
Daelim H&L Plavis N Aromatic Polyimide, Non-Filled, Machined Parts
| Category | Polymer , Thermoset , Polyimide, TS |
| Manufacturer | Daelim H&L Super Engineering Plastics |
| Trade Name | Plavis |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Daelim H&L Plavis N Aromatic Polyimide, Non-Filled, Machined Parts.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Superior chemical property, very high radiation resistance, electrical and thermal property, low outgassing and superior physical propertyInformation provided by Daelim H&L
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.95 % | 0.95 % | 50% RH; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 - 100 | 85 - 100 | ASTM D785 |
| Tensile Strength, Ultimate | 50.4 MPa @Temperature 260 °C |
7310 psi @Temperature 500 °F |
ASTM D1708 |
| 92.1 MPa @Temperature 23.0 °C |
13400 psi @Temperature 73.4 °F |
ASTM D1708 | |
| Tensile Strength, Yield | 26.4 MPa @Strain 1.00 % |
3830 psi @Strain 1.00 % |
ASTM D95 |
| 165.1 MPa @Strain 10.0 % |
23950 psi @Strain 10.0 % |
ASTM D95 | |
| Elongation at Break | 8.9 % @Temperature 260 °C |
8.9 % @Temperature 500 °F |
ASTM D1708 |
| 12.8 % @Temperature 23.0 °C |
12.8 % @Temperature 73.4 °F |
ASTM D1708 | |
| Flexural Strength | 65.1 MPa @Temperature 260 °C |
9440 psi @Temperature 500 °F |
ASTM D790 |
| 125.6 MPa @Temperature 23.0 °C |
18220 psi @Temperature 73.4 °F |
ASTM D790 | |
| Flexural Modulus | 1.83 GPa @Temperature 260 °C |
266 ksi @Temperature 500 °F |
ASTM D790 |
| 3.1559 GPa @Temperature 23.0 °C |
457.72 ksi @Temperature 73.4 °F |
ASTM D790 | |
| Compressive Modulus | 2.7213 GPa @Temperature 23.0 °C |
394.69 ksi @Temperature 73.4 °F |
ASTM D695 |
| Shear Strength | 90.252 MPa @Temperature 23.0 °C |
13090 psi @Temperature 73.4 °F |
ASTM D732 |
| Izod Impact, Notched (ISO) | 5.1012 kJ/m² | 2.4278 ft-lb/in² | ASTM D256 |
| Coefficient of Friction | 0.24 | 0.24 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 5.60 µm/m-°C @Temperature 23.0 - 260 °C |
3.11 µin/in-°F @Temperature 73.4 - 500 °F |
ASTM D696 |
| Specific Heat Capacity | 1.17 J/g-°C | 0.280 BTU/lb-°F | |
| Decomposition Temperature | 616 °C | 1140 °F | |
| Oxygen Index | 55 % | 55 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 - 1.00e+16 ohm-cm @Temperature 23.0 °C |
1.00e+15 - 1.00e+16 ohm-cm @Temperature 73.4 °F |
ASTM D257 |
| Dissipation Factor | 0.0036 @Frequency 1.00e+6 Hz, Temperature 23.0 °C |
0.0036 @Frequency 1.00e+6 Hz, Temperature 73.4 °F |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| 50% Weight Reduction Time (Minutes) | 240 |
Users viewing this material also viewed the following:
- MV Labs GE800 GeO2 Germanium(IV) oxide
- Nylene® 724 Nylon 6
- Nilit Nilamon B3 H7 GK 35 15% Glass Fiber, 25% Mineral Reinforced PA6
- Kennametal Stellite Deloro® 22 Nickel Alloy
- LG Chemical Lupox® GP2306FB PBT+GF30%
- Borealis FT5232 Low Density Polyethylene
- A. Schulman FORMION™ FI 555-31 Recycled Ionomer
- A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66
- Fainplast Compounds MRT 256/G Medical Rigid PVC, Injection Molding
- SABIC Innovative Plastics Xylex FXY391DF PC+POLYESTER (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved