Chosun Refractories HACT-165 High Alumina Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories HACT-165 High Alumina Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.0024525 - 0.0063765 GPa @Temperature 1000 °C, Time 10800 sec |
0.35571 - 0.92485 ksi @Temperature 1830 °F, Time 3.00 hour |
|
| 0.002943 - 0.006867 GPa @Temperature 1350 °C, Time 10800 sec |
0.4269 - 0.9960 ksi @Temperature 2460 °F, Time 3.00 hour |
||
| 0.002943 - 0.006867 GPa @Temperature 110 °C, Time 86400 sec |
0.4269 - 0.9960 ksi @Temperature 230 °F, Time 24.0 hour |
||
| 0.004905 - 0.008829 GPa @Temperature 1500 °C, Time 10800 sec |
0.7114 - 1.281 ksi @Temperature 2730 °F, Time 3.00 hour |
||
| Compressive Strength | 14.7 - 19.6 MPa @Temperature 1000 °C, Time 10800 sec |
2130 - 2840 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength |
| 19.6 - 29.4 MPa @Temperature 1350 °C, Time 10800 sec |
2840 - 4270 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 19.6 - 29.4 MPa @Temperature 110 °C, Time 86400 sec |
2840 - 4270 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength | |
| 29.4 - 39.2 MPa @Temperature 1500 °C, Time 10800 sec |
4270 - 5690 psi @Temperature 2730 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.7560 W/m-K @Temperature 260 °C |
5.238 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.8724 W/m-K @Temperature 540 °C |
6.044 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| 1.0003 W/m-K @Temperature 800 °C |
6.9309 BTU-in/hr-ft²-°F @Temperature 1470 °F |
||
| Maximum Service Temperature, Air | 1650 °C | 3000 °F | limited |
| Shrinkage | -0.400 % @Temperature 1500 °C, Time 10800 sec |
-0.400 % @Temperature 2730 °F, Time 3.00 hour |
|
| -0.300 % @Temperature 1350 °C, Time 10800 sec |
-0.300 % @Temperature 2460 °F, Time 3.00 hour |
||
| -0.0600 % @Temperature 110 °C, Time 86400 sec |
-0.0600 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 58 % | 58 % | |
| SiO2 | 36 % | 36 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Material Required for Estimating(kg/?) | 2,250 | |
| Water Required for Casting(%) | 10.0 |
Users viewing this material also viewed the following:
- MV Labs MN300 MnCO3 Manganese(II) carbonate
- Rostone Rosite® C200BS ESD SMC, Conductive Thermoset Polyester, 10% Glass Reinforced (discontinued **)
- PolyOne Lubri-Tech™ NL-15KV/05M Nylon 6/12 - 15% Kevlar Fiber - 5% MoS2 (discontinued **)
- Kazanorgsintez 297-285 High Density Polyethylene Composite
- Shin-Etsu Silicones LIMSâ„¢ KE1950-30A/B Elastomer
- Saint-Gobain Vendflow® E-70-V-CE Taste Barrier Tubing Formulation
- A. Schulman POLYBATCH™ Norwegian Wood 60242U/3 Concentrate Based In LLDPE
- Diamond Polymers Softflex® 1302 Thermoplastic Elastomer Alloy
- Aclo Accutech Nylon 6 NY0730G10L Glass Reinforced
- ExxonMobil Mobil Pegasus 710 40
Copyright © lookpolymers.com All Rights Reserved