Chosun Refractories HACT-160 High Alumina Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories HACT-160 High Alumina Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.0025506 - 0.005886 GPa @Temperature 1000 °C, Time 10800 sec |
0.36994 - 0.8537 ksi @Temperature 1830 °F, Time 3.00 hour |
|
| 0.0024525 - 0.0063765 GPa @Temperature 1350 °C, Time 10800 sec |
0.35571 - 0.92485 ksi @Temperature 2460 °F, Time 3.00 hour |
||
| 0.0024525 - 0.0063765 GPa @Temperature 110 °C, Time 86400 sec |
0.35571 - 0.92485 ksi @Temperature 230 °F, Time 24.0 hour |
||
| Compressive Strength | 9.81 - 19.6 MPa @Temperature 1000 °C, Time 10800 sec |
1420 - 2840 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength |
| 14.7 - 24.5 MPa @Temperature 1350 °C, Time 10800 sec |
2130 - 3560 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 14.7 - 24.5 MPa @Temperature 110 °C, Time 86400 sec |
2130 - 3560 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.77931 W/m-K @Temperature 260 °C |
5.3997 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.79094 W/m-K @Temperature 540 °C |
5.4803 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| Maximum Service Temperature, Air | 1600 °C | 2910 °F | limited |
| Shrinkage | -0.100 % @Temperature 1350 °C, Time 10800 sec |
-0.100 % @Temperature 2460 °F, Time 3.00 hour |
|
| -0.0600 % @Temperature 110 °C, Time 86400 sec |
-0.0600 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 53 % | 53 % | |
| SiO2 | 40 % | 40 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Material Required for Estimating(kg/?) | 2,220 | |
| Water Required for Casting(%) | 10.0 |
Users viewing this material also viewed the following:
- Pasargad Polymer Peyvand Pasalen 3P-H3230B Polypropylene, 30% Mineral Filled Reinforced
- SABIC Innovative Plastics Lexan® LUX9136C PC COPOLYMER (Asia Pacific)
- Silberline EternaBrite® 651-PA
- A. Schulman POLYBATCH™ Forest Green LL30318 Concentrate Based In LLDPE
- Chesterton ARC S7 High Temperature & Chemical Resistant Novolac Vinyl Ester Coating
- Covestro Bayblend® KU 2-1514* Polycarbonate + ABS, Flame Retardant Grade
- Eurostar Staramide PB (03 - 10) PA66, Glass Bead Filled, Injection Molding Resin
- Aclo Accucomp Polyacetal (POM) ACE092L Medium Viscosity
- Addiplast Addilene H 542 Polypropylene Homopolymer
- Aremco Aremco-Seal™ 529 High Temperature Specialty Coatings Silicone
Copyright © lookpolymers.com All Rights Reserved