Chevron Phillips Marlex® C590 High Density Polyethylene (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chevron Phillips Marlex® C590 High Density Polyethylene
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Density PolyethyleneData provided by Chevron Phillips Chemical Company, LP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | 80 hour | 80 hour | Condition A, F<sub>50</sub>, ASTM D1693; Bottle ESCR: 250, ASTM D2561 |
| Melt Flow | 21 g/10 min | 21 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | 2 in per min; ASTM D638 Type IV |
| Flexural Modulus | 1.378 GPa | 199.9 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -180 °C | <= -292 °F | ASTM D746 |
Users viewing this material also viewed the following:
- Solvay Engineered Polymers SEQUEL® 2330 Engineered Polyolefin (discontinued **)
- LG Chemical Lupox® HV1005S PBT
- Michelman® CleanGrip® 111 Alumina based, nonskid coating
- Henkel Turco Ridoline 4355 Cleaner
- Teknor Apex APEX® 97-G0029C-82 Polyvinyl Chloride, Flexible
- A. Schulman POLYFORT™ FPP 2181HU High Flow, Fortified, Impact Resistant Polypropylene
- A. Schulman FORMION™ FI 401 Ionomer
- Asahi Kasei Thermylene® P-40TC-8100 Chemically Coupled Polypropylene Compound, 40% Talc Filled
Copyright © lookpolymers.com All Rights Reserved