Chevron Phillips HiD® 9607D HDPE Cast Film Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips HiD® 9607D HDPE Cast Film Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics: Very Low Gel Levels, Produces Very "Clear" Film, Draws to Thin Gauges, Low Taste and Odor Transfer, Excellent MVTR for a Chill Cast Film, Excellent Processability, Excellent Optical PropertiesApplications:Coextrusions, Overwrap, Food Packaging, Moisture Sensitive PackagingFilm properties below based on film thickness of 31.8 µm.Data provided by Chevron Chemical.

Physical Properties	Metric	English	Comments
Density	0.962 g/cc	0.0348 lb/in³	ASTM D1505
Moisture Vapor Transmission	0.170 cc-mm/m²-24hr-atm	0.432 cc-mil/100 in²-24hr-atm	ASTM F1249
Melt Flow	6.0 g/10 min	6.0 g/10 min	Condition E; ASTM D 1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	870 %	870 %	ASTM D882
Film Elongation at Break, TD	790 %	790 %	ASTM D882
Secant Modulus, MD	0.760 GPa	110 ksi	ASTM D882
Secant Modulus, TD	0.840 GPa	122 ksi	ASTM D882
Elmendorf Tear Strength, MD	1.38 g/micron	35.0 g/mil	Notched; ASTM D1922
Elmendorf Tear Strength, TD	3.94 g/micron	100 g/mil	ASTM D1922
Dart Drop	1.30 g/micron	33.0 g/mil	1.5 in. dart/26 in. drop height; ASTM D 1709
Film Tensile Strength at Break, MD	29.0 MPa	4210 psi	ASTM D882
Film Tensile Strength at Break, TD	23.0 MPa	3340 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	11 %	11 %	ASTM D2457
Gloss	120 %	120 %	at 60°. ASTM D 2457