Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
Manufacturer | Consolidated Polymer Technologies |
Trade Name | C-Flex® |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | CPT C-Flex® R70-003 Opaque Biocompatible TPE.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D 792 |
Linear Mold Shrinkage | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | |
Melt Flow | 7.1 g/10 min | 7.1 g/10 min | Condition D; ASTM D 1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Shore A | 76 | 76 | 1 sec.; ASTM D 2240 |
Tensile Strength at Break | 8.48 MPa | 1230 psi | ASTM D 412 |
Elongation at Break | 632 % | 632 % | ASTM D 412 |
100% Modulus | 0.00234 GPa | 0.340 ksi | ASTM D 412 |
300% Modulus | 0.00448 GPa | 0.650 ksi | ASTM D 412 |
Tear Strength | 34.4 kN/m | 196 pli | Notched, Die B; ASTM D 624 |
54.3 kN/m | 310 pli | Die C; ASTM D 624 | |
Taber Abrasion, mg/1000 Cycles | 12 | 12 | Federal Test Method Standard, 405 |
Compression Set | 25 % | 25 % | 23°C; ASTM D 412 |
70 % @Temperature 70.0 °C |
70 % @Temperature 158 °F |
ASTM D 412 | |
Tensile Set | 37 % | 37 % | at 300% elongation; ASTM D 412 |
110 % | 110 % | at break; ASTM D 412 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Brittleness Temperature | -73.3 °C | -100 °F | ASTM D 746 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Processing Temperature | 163 - 204 °C | 325 - 400 °F | Extrusion Temperature |
Middle Barrel Temperature | 149 - 218 °C | 300 - 425 °F | Injection molding cylinder temperature |
Drying Temperature | 65.6 - 93.3 °C | 150 - 200 °F | Desiccant type |
Injection Pressure | 2.07 - 6.89 MPa | 300 - 1000 psi |
Descriptive Properties | Value | Comments |
---|---|---|
Sterilization methods: | Steam/Autoclave, Cobalt 60, Ethylene Oxide |