Braskem LQ 0518/30 LLDPE Blown Film Extrusion Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem LQ 0518/30 LLDPE Blown Film Extrusion Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
38µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Heavy duty bags; shrink film. Information provided by Braskem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 0.55 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.55 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 885 % | 885 % | ASTM D882 |
| Film Elongation at Break, TD | 1088 % | 1088 % | ASTM D882 |
| Secant Modulus, MD | 0.266 GPa | 38.6 ksi | 1%; ASTM D882 |
| Secant Modulus, TD | 0.320 GPa | 46.4 ksi | 1%; ASTM D882 |
| Coefficient of Friction | 0.67 | 0.67 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 10.6 g/micron | 269 g/mil | ASTM 1922 |
| Elmendorf Tear Strength, TD | 25.4 g/micron | 645 g/mil | ASTM 1922 |
| Dart Drop | 3.60 g/micron | 91.4 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 57.0 MPa | 8270 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 42.0 MPa | 6090 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 13.4 % | 13.4 % | ASTM D1003 |
| Gloss | 8.4 % | 8.4 % | 60° angle; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Antiblock and PPA | |
| Minimum Recommended Thickness | 45 µm |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable JG513GO Polyvinyl Chloride, Flexible (PVC, Flexible)
- RheTech Products FT4802-690UVA Thermoplastic Polyolefin, UV Stabilized, HS5 Medium Dark Neutral
- Ravago Manufacturing Americas Hylac® FR134 ABS
- Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 7% Plasticizer (discontinued **)
- A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene
- Dow Corning LSPBK25 SILICONE MASTERBATCH BLACK
- Aclo Accutech Polycarbonate POL050G20L Glass Reinforced
- Applied Composites 150 Polyester SMC
- Henkel Fixodine Z Surface Conditioner
Copyright © lookpolymers.com All Rights Reserved