Braskem LQ 0518/21 AF LLDPE Blown Film Extrusion Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem LQ 0518/21 AF LLDPE Blown Film Extrusion Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
38µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Coextruded film for automatic packaging (FFS). Information provided by Braskem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 0.55 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.55 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 655 % | 655 % | ASTM D882 |
| Film Elongation at Break, TD | 1002 % | 1002 % | ASTM D882 |
| Secant Modulus, MD | 0.278 GPa | 40.3 ksi | 1%; ASTM D882 |
| Secant Modulus, TD | 0.288 GPa | 41.8 ksi | 1%; ASTM D882 |
| Coefficient of Friction | 0.17 | 0.17 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 9.20 g/micron | 234 g/mil | ASTM 1922 |
| Elmendorf Tear Strength, TD | 27.7 g/micron | 704 g/mil | ASTM 1922 |
| Dart Drop | 4.92 g/micron | 125 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 34.7 MPa | 5030 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 29.1 MPa | 4220 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 12.4 % | 12.4 % | ASTM D1003 |
| Gloss | 9.0 % | 9.0 % | 60° angle; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Antiblock, Slip, and PPA | |
| Minimum Recommended Thickness | 40 µm |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WELB406L Polyvinyl Chloride, Flexible (PVC, Flexible)
- Ovation Polymers Nemcon™ H PC DP111/X1 Polycarbonate
- SABIC Innovative Plastics Lexan® 955 PC (Asia Pacific)
- Solvay MIRATAINE® CBS-LR Surfactant
- A. Schulman POLYBATCH™ Lattice Green 30155U Concentrate Based In LLDPE
- 3M FP022202 White Polypropylene Label Products
- Advanced Polymer Alloys DuraGrip™ DGR 6040 NCHT Thermoplastic Elastomer (TPE)
- Reade Advanced Materials Wood's Metal Alloy (Sn + Pb + Bi + Cd)
Copyright © lookpolymers.com All Rights Reserved