- Braskem LHB118/21AF Blown Film Extrusion Linear Low Density Polyethylene
Braskem LHB118/21AF Blown Film Extrusion Linear Low Density Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem LHB118/21AF Blown Film Extrusion Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Frozen chicken packages; Meat-based frozen packages.Additives: Antiblock, D, PPA, PEBDInformation provided by Braskem.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.917 g/cc | 0.917 g/cc | ASTM D1505/D792 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 1000 % | 1000 % | ASTM D882 |
| Film Elongation at Break, TD | 1280 % | 1280 % | ASTM D882 |
| Elmendorf Tear Strength MD | 80 g | 80 g | gF; ASTM D1922 |
| Elmendorf Tear Strength TD | 560 g | 560 g | gF; ASTM D1922 |
| Dart Drop Test | 100 g | 0.221 lb | gF/50%f; ASTM D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| 1% Secant Modulus, MD | 180 MPa | 26100 psi | ASTM D882 |
| 1% Secant Modulus, TD | 210 MPa | 30500 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 12 % @Thickness 0.0380 mm |
12 % @Thickness 0.00150 in |
ASTM D1003 |
| Gloss | 98 % @Thickness 0.0380 mm |
98 % @Thickness 0.00150 in |
60°; ASTM D2457 |
Users viewing this material also viewed the following:
- Polymer Resources NY66-G43-[color]-H Nylon 66, 43% Glass Reinforced, Heat Stabilized
- PolyOne Geon™ Vinyl Flexible XV 1144 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Kingfa FRHIPS-220 Flame Retardant Polystyrene
- Lubrizol Advanced Materials Pearlthane® 11T85 Polycaprolactone Copolyester based TPU
- Gwent Electronic Materials D2060131D1 Dielectric Paste
- Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F)
- Samsung Cheil Industries Starex® LX-0971 S ABS, Unreinforced Metallic-Look
- Eastman Eastar BR001 Copolyester
- DSM Novamid® 2030J PA666
- 3M 468MP High Performance Adhesive Transfer Tapes with Adhesive 200MP
Copyright © lookpolymers.com All Rights Reserved