Braskem LF 0720/20 AF LLDPE Blown Film Extrusion Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem LF 0720/20 AF LLDPE Blown Film Extrusion Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
38µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Heavy duty bags; "liners"; general purpose; HDPE and LDPE blends. Information provided by Braskem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 958 % | 958 % | ASTM D882 |
| Film Elongation at Break, TD | 1190 % | 1190 % | ASTM D882 |
| Secant Modulus, MD | 0.175 GPa | 25.4 ksi | 1%; ASTM D882 |
| Secant Modulus, TD | 0.205 GPa | 29.7 ksi | 1%; ASTM D882 |
| Coefficient of Friction | 0.70 | 0.70 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 3.30 g/micron | 83.8 g/mil | ASTM 1922 |
| Elmendorf Tear Strength, TD | 14.6 g/micron | 371 g/mil | ASTM 1922 |
| Dart Drop | 2.55 g/micron | 64.8 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 38.0 MPa | 5510 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 8.8 % | 8.8 % | ASTM D1003 |
| Gloss | 10.7 % | 10.7 % | 60° angle; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Antiblock and PPA | |
| Minimum Recommended Thickness | 30 µm |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® BD 30 Low Density Polyethylene - Blow Molding
- Lehmann & Voss LUVOCOM® 1105-7460/BL5019 PEEK, with glass fiber
- LATI Lastilac RT K/10 ABS, 10% Carbon Fiber Reinforced
- Lehmann & Voss LUVOCOM® 1105/GF/40/BK-1 PEEK, with glass fiber
- Lehmann & Voss LUVOCOM® 1105-7327 PEEK, with glass fiber
- Samsung Cheil Industries Starex® BF-0930 MABS, Unreinforced Scratch Resistant
- CeramTec Sonox® P502 Piezoceramic
- Dynasol Calprene® 487 Thermoplastic Rubber SBS Oil extended
- Braskem GF5250 HDPE Blow Molding Polyethylene Copolymer
Copyright © lookpolymers.com All Rights Reserved