Braskem Flexus® 9200 LLDPE Blown Film Extrusion

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer Braskem
Trade Name Flexus®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem Flexus® 9200 LLDPE Blown Film Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Flexus 9200 is a LLDPE hexene copolymer produced through metallocene catalyst which presents excellent impact and puncture strength, beyond a differential sealing performance comparing with another typical LLDPE. It processing aid and antioxidant additives25µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications:Heavy-duty bags; liners, LDPE and HDPE blends; packages for general use. Information provided by Braskem
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ASTM D1505
Thickness 25.0 microns
0.984 mil
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 1010 %
1010 %
ASTM D882
Film Elongation at Break, TD 1210 %
1210 %
ASTM D882
Secant Modulus, MD 0.130 GPa
18.9 ksi
1%, Flexural; ASTM D882
Secant Modulus, TD 0.150 GPa
21.8 ksi
1%, Flexural; ASTM D882
Coefficient of Friction 0.70
0.70
ASTM D1894
Elmendorf Tear Strength, MD 9.60 g/micron
244 g/mil
ASTM 1922
Elmendorf Tear Strength, TD 15.2 g/micron
386 g/mil
ASTM 1922
Dart Drop >= 34.0 g/micron
>= 864 g/mil
ASTM D1709
Heat Seal Strength Initiation Temperature 99.0 °C
210 °F
Sealing Initial Temperature
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM D1003
Gloss 120 %
120 %
ASTM D2457
Descriptive Properties Value Comments
Additives PPA
Puncture Strength 30 J/mm
ASTM D5748