- Beijing Chemical Industry KAIFA® 301-G15 PBT Resin
Beijing Chemical Industry KAIFA® 301-G15 PBT Resin
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® 301-G15 PBT Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 88.0 MPa | 12800 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 140 MPa | 20300 psi | ASTM D790 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm @Thickness 3.20 mm |
0.937 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 1e+6 Hz |
3.3 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Lubriplate APG-90 Petroleum-Based Gear, Bearing, & Recirculating Oil
- SABIC Innovative Plastics SABIC PPCOMPOUND 5521 PP
- Borealis Daplen™ EF341AE Polypropylene TPO Compound
- A. Schulman LP544-01 High-Density Copolymer Polyethylene
- Cheng Yu Plastic T888G15 PBT, 15% Glass Fiber
- Ashley Polymers Ashlene® 940H Nylon 11
- Von Roll Isola IMI Varnish 3405 Polyester Varnish for Electrical Insulation
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Hardened + 649°C (1200°F) Temper
- SABIC Innovative Plastics Cycoloy® C1100 PC+ABS (Europe-Africa-Middle East)
- A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved