- Barlog Plastics KEBATRON L2040G3 PPS, linear, 40% glass fiber reinforced, reduced residual chlorine
Barlog Plastics KEBATRON L2040G3 PPS, linear, 40% glass fiber reinforced, reduced residual chlorine
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBATRON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBATRON L2040G3 PPS, linear, 40% glass fiber reinforced, reduced residual chlorine.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPS-GF40Information provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Water Absorption | 0.020 % | 0.020 % | similar to ISO 62 test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527-1 |
| Elongation at Break | 1.2 % | 1.2 % | ISO 527-1 |
| Tensile Modulus | 14.5 GPa | 2100 ksi | ISO 527-1 |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179-1eU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C | 12.2 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 285 °C | 545 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL Registered; IEC 60695-11-10 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | PPS-GF40 |
Users viewing this material also viewed the following:
- Polykemi AB SCANAMID 66 A12^ F25 NH10 Nylon 66, Glass Fiber Reinforced, Flame Retardant
- Polymer Resources TP-FRG7.5 Polybutylene Terephthalate, 7 1/2 % Glass Reinforced, Flame Retardant
- Covestro Apec® DP9-9354 High-Heat Polycarbonate, Flame-Retardant (discontinued **)
- Haysite 46000 Polyester SMC, 30% Glass Reinforced
- Techmer ES Plaslube® NY-1/TF/20 BK223 PA66
- Techmer ES HiFill® PBT GF20 20% Glass Filled
- 3M Scotchcal™ ElectroCut™ 7125-47 Graphic Film
- 3M SJ-2FB Cold Shrink Foldback Splice Jacket Kits
- Bulk Molding Compounds BMC T40(18)-LS Die Casting Replacement Grade Molding Compound
- Addiplast Addinyl B2H G15 Flame Retardant Nylon 6, 15% Glass Bead
Copyright © lookpolymers.com All Rights Reserved