BNZ Materials Color B Insulating Firebrick (French Grade)

Category Ceramic , Oxide , Aluminum Oxide
Manufacturer BNZ Materials, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BNZ Materials Color B Insulating Firebrick (French Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BNZ produces many types of Insulating Fire Brick (IFB) for use in applications from 2,000°F (1,093°C) to 3,200°F (1,760°C). Each type is formulated to meet specific thermal and physical requirements and after firing is machined to precise tolerances. Made from high purity refractory clays and other ceramic raw materials, these IFB contain a carefully graded organic filler which is burned out during manufacture to give a uniform controlled pore structure.Information provided by BNZ Materials Inc.
Physical Properties Metric English Comments
Density 0.900 g/cc
0.0325 lb/in³
ASTM C134
Mechanical Properties Metric English Comments
Compressive Strength 4.00 MPa
580 psi
Cold Crush Strength; ASTM C133
Thermal Properties Metric English Comments
CTE, linear 6.30 µm/m-°C

@Temperature 20.0 - 1000 °C
3.50 µin/in-°F

@Temperature 68.0 - 1830 °F
Thermal Conductivity 0.230 W/m-K

@Temperature 200 °C
1.60 BTU-in/hr-ft²-°F

@Temperature 392 °F
ASTM C182
0.270 W/m-K

@Temperature 400 °C
1.87 BTU-in/hr-ft²-°F

@Temperature 752 °F
ASTM C182
0.300 W/m-K

@Temperature 600 °C
2.08 BTU-in/hr-ft²-°F

@Temperature 1110 °F
ASTM C182
0.350 W/m-K

@Temperature 800 °C
2.43 BTU-in/hr-ft²-°F

@Temperature 1470 °F
ASTM C182
0.400 W/m-K

@Temperature 1000 °C
2.78 BTU-in/hr-ft²-°F

@Temperature 1830 °F
ASTM C182
Maximum Service Temperature, Air 1350 °C
2460 °F
Shrinkage 0.50 %

@Temperature 1350 °C,
Time 43200 sec
0.50 %

@Temperature 2460 °F,
Time 12.0 hour
Permanent Linear Change; ASTM C210
Descriptive Properties Value Comments
Composition (%) 0.6
CaO + MgO
2.3
Fe<sub>2</sub>O<sub>3</sub> + TiO<sub>2</sub>
4.5
Na<sub>2</sub>O + K<sub>2</sub>O
92.4
Al<sub>2</sub>O<sub>3</sub> + SiO<sub>2</sub>